マグネシウム合金AZ31Bろう付用フラックスおよびろう材の開発
スポンサーリンク
概要
- 論文の詳細を見る
This study was carried out to develop the flux and filler metals that enabled brazing a magnesium alloy plate of AZ31B at the temperature lower than 490℃. The following results were obtained in this study. The newly developed flux that consisted of CaCl2, LiCl and NaCl containing Ca ion and Liion could successfully removed the oxide film from the magnesium alloy surface at around 450℃, and enabled us to braze the magnesium alloy at the temperature lower than 490℃. In addition, we were successful in developing the brazing filler metal with the melting temperature lower than 480℃ that consisted of magnesium and indium as a main component and a small amount of zinc to lower the melting temperature. A joint with high strength equivalent to the base metal one was achieved using the above flux and the filler metal with little zinc, and the joint strength decreased with the increase in the zinc content.
- 溶接学会の論文
- 2004-00-00
溶接学会 | 論文
- 研究者・技術者に必須の「効果的技術英文の組み立て方」 : テクニカル・ライティング練習張
- 補修溶接の採否の決定と施工上のポイント-2-圧力容器
- これからの溶接・接合技術の展開と提言
- 破壊靱性と継手破壊強度
- ものづくりを革新するレーザ溶接