回転ピンによる鉄鋼とアルミニウム合金の固相接合 : 回転ピンによる異種材料の固相接合(第1報)
スポンサーリンク
概要
- 論文の詳細を見る
Authors tried to butt-weld a mild steel plate to an aluminum alloy plate by the solid slate welding using a rotating pin. This study investigated the effects of a pin rotation speed, the position for the pin axis to be inserted and the pin diameter on the tensile strength and the microstructure of the joint. The main results obtained are as follows: Butt-welding of a steel plate to an aluminum alloy plate was easily and successfully achieved. The maximum tensile strength of the joint was about 86% of that of the aluminum alloy base metal. Many fragments of the steel were scattered in the aluminum alloy matrix, and fracture tended to occur along the interface between the fragment and the aluminum matrix. A small amount of intermetallic compounds was formed at the upper pan of the steel/aluminum interface, while no intermetallic compounds were observed in the middle and bottom parts of the interface. A little intermetallic compound was also often formed at the interface between the steel fragments and the aluminum matrix. The regions where the intermetallic compounds formed seem to be fracture paths in a joint.
- 溶接学会の論文
- 2004-00-00
溶接学会 | 論文
- 研究者・技術者に必須の「効果的技術英文の組み立て方」 : テクニカル・ライティング練習張
- 補修溶接の採否の決定と施工上のポイント-2-圧力容器
- これからの溶接・接合技術の展開と提言
- 破壊靱性と継手破壊強度
- ものづくりを革新するレーザ溶接