ホーンを介した水中超音波照射による金属材料表面への圧縮残留応力の付与 : 液中超音波照射による材料の表面改質(第1報)
スポンサーリンク
概要
- 論文の詳細を見る
Ultrasonic wave of 19.5 kHz frequency oscillated with an ultrasonic transducer and amplified with a step type horn was irradiated on metal surfaces in water to introduce compressive residual stress. Slight plastic deformation occurred at the surface region of pure metal such as Cu and compressive residual stress was introduced. It seemed that the plastically deformed depth from the surface corresponded approximately to the region where the compressive residual stress is extended from the surface. The higher compressive residual stress could be introduced into the surface of Cu-Zn brass and SUS304 stainless steel because work-hardening was simultaneously induced to those alloys. Furthermore, since martensitic transformation was induced by the plastic deformation in the case of SUS304, the lager compressive residual stress could be introduced more deeply into the surface region. The residual stress of SUS304 surface reached to the maximum value of 574 MPa by irradiating for 5 min and the stress extended to the depth of about 170μm from the surface.
- 溶接学会の論文
- 2004-00-00
溶接学会 | 論文
- 研究者・技術者に必須の「効果的技術英文の組み立て方」 : テクニカル・ライティング練習張
- 補修溶接の採否の決定と施工上のポイント-2-圧力容器
- これからの溶接・接合技術の展開と提言
- 破壊靱性と継手破壊強度
- ものづくりを革新するレーザ溶接