Enhanced activity and stability of Pt/C fuel cell anodes by the modification with ruthenium-oxide nanosheets
スポンサーリンク
概要
- 論文の詳細を見る
Ruthenium-oxide nanosheet (RuO(2)ns) crystallites with thickness less than 1 nm were prepared via chemical exfoliation of a layered potassium ruthenate and deposited onto carbon supported platinum (Pt/C) as a potential co-catalyst for fuel cell anode catalysts. The electrocatalytic activity towards carbon monoxide and methanol oxidation was studied at various temperatures for different RuO(2)ns loadings. An increase in electrocatalytic activity was evidenced at temperatures above 40 degrees C, while little enhancement in activity was observed at room temperature. The RuO(2)ns modified Pt/C catalyst with composition of RuO2:Pt=0.5:1 (molar ratio) exhibited the highest methanol oxidation activity. CO-stripping-voltammetry revealed that RuO(2)ns promotes oxidation of adsorbed CO on Pt. In addition to the enhanced initial activity, the RuO(2)ns modified Pt/C catalyst exhibited improved stability compared to pristine Pt/C against consecutive potential cycling tests.
- PERGAMON-ELSEVIER SCIENCE LTDの論文
- 2010-01-01
著者
-
Takasu Y
Department Of Materials And Chemical Engineering Faculty Of Textile Science And Technology Shinshu U
-
Sugimoto Wataru
Department Of Materials And Chemical Engineering Faculty Of Textile Science And Technology Shinshu U
-
Sugimoto Wataru
Department Of Materials And Chemical Engineering Faculty Of Textile Science And Technology Shinshu U
-
Takasu Yoshio
Department Of Materials And Chemical Engineering Faculty Of Textile Science And Technology Shinshu University
関連論文
- Catalytic Linear Grooving of Graphite Surface Layers by Pt, Ru, and PtRu Nanoparticles
- Differential Expression of Two Cytochrome P450s Involved in the Biosynthesis of Flavones and Anthocyanins in Chemo-Varietal Forms of Perilla frutescens
- cDNA Cloning and Gene Expression of Anthocyanidin Synthase from Torenia fournieri
- Preparation of Nitrogen-doped Anatase Titania by Treatment of Layered Titania/Isostearate Nanocomposite with Aqueous Ammonia
- Microporous Structure of Alumina Prepared by a Salt Catalytic Sol-Gel Process
- Microporous Structure of Titanium Oxide Prepared by a Salt Catalytic Sol-Gel Process
- Photochromism of Titanium Oxide Gels Prepared by the Salt-Catalytic Sol-Gel Process
- Preparation of a UV-absorbed Transparent Monolithic Titanium Oxide Gel by the Catalytic Sol-Gel Process with a Phenanthroline Hydrochloride Catalyst
- Catalytic Excavation and Graphitization of Activated Carbon by Cobalt Nanoparticles
- Effect of the Crystal Plane on the Catalytic Etching Behavior of Diamond Crystallites by Cobalt Nanoparticles
- Incorporation of Ethylenediamine as a Bi-layer in the Interlayer Space of Tetratitanic Acid by Re-stacking Exfoliated Nanosheets
- Effects of the Addition of Calcium on the Pseudocapacitance of Ruthenium Oxide Electrodes
- Pseudocapacitance of Molybdenum Oxide Particles Highly Dispersed on Glassy Carbon Surface
- Extremely High Pseudo-Capacitance of RuO_2 Highly Dispersed on Glassy Carbon
- Preparation of Ultrafine Ruthenium Oxide Particles with Ammonium Hydrogencarbonate (論文特集号 電解科学技術の進展)
- A New Method for the Preparation of a Glassy Carbon - Supported Ultrafine Gold Particle Electrode
- Self-Embedment of Small Rectangular Parallelepiped Platinum Particle Array in Etch Pits on {100} Planes of Diamond Crystallites
- Enhanced activity and stability of Pt/C fuel cell anodes by the modification with ruthenium-oxide nanosheets
- Oxygen reduction characteristics of several valve metal oxide electrodes in HClO(4) solution