The Influence of Applied Stress Ratio on Fatigue Strength of TiN-coated Carbon Steel
スポンサーリンク
概要
- 論文の詳細を見る
The influence of applied stress ratio on the fatigue strength of carbon steel coated with TiN was studied on the basis of measurement of crack initiation with the D. C. potential method. Fatigue tests were performed under the stress ratios of R=0 and -1 in air using the round notched specimens of O.37%C steel, JIS S35C, normalized and coated with TiN by physical vapor deposition (PVD) and chemical vapor deposition (CVD). From the experimental results, increase in fatigue strength was observed in TiN-coated specimens under test conditions of R=-1, as compared with that of uncoated specimens. However, the fatigue life of specimens coated by PVD was decreased under the tests of R=0, except for the region of low stress amplitude. Also, the fatigue life of specimens coated by CVD under test conditions of R=0 was smaller than that of uncoated specimens. The difference in fatigue life with applied stress ratio is explained by the fracture behavior of coating film on the specimen surface.
- 社団法人日本機械学会の論文
- 1992-07-00
社団法人日本機械学会 | 論文
- 〔計測器(d)〕 静電容量式半導体加速度センサと試験装置(最近のダンピング計測技術の動向について(計測器メーカーによる講演とデモンストレーション))(最近のダンピング計測技術の動向について)
- 1807 粒状路盤の塑性変形がコンクリート舗装の力学的挙動に及ぼす影響(OS-18B 舗装の構造診断,OS-18 交通施設と計算力学)
- 1P2-N-059 アドホックワイヤレスネットワークに基づくライフログを利用した機器操作支援システム(人間機械協調2,生活を支援するロボメカ技術のメガインテグレーション)
- 1A1-N-093 酸素消費率に合わせてコントロールされる呼吸器・循環器統合シミュレータ(デジタルヒューマン1,生活を支援するロボメカ技術のメガインテグレーション)
- 仮想ロボット化記述を用いた複数台ロボットによる協調搬送(空間知能化2)