Microstructure and analysis of oxide scales formed on Cr-Si-Ni compacts in air and H2O-containing atmosphere
スポンサーリンク
概要
- 論文の詳細を見る
The purpose of this study was to characterize the oxide scales formed on various Cr-Si-Ni compacts at 1273 K in air and H2O-containing atmosphere by TEM. It was found that CrSi2-(5-20) mass%Ni compacts form double layer scales, consisting of an outer Cr2O3 layer and an inner SiO2 layer. The oxide scale changed from SiO2- to Cr2O3-based scale with an increase in the Ni concentration. However, it was observed that the oxide scale formed in H2O-containing atmospheres showed local SiO2 growth into the substrate. This result suggests that the inward oxidant diffusion promotes the local growth of SiO2 in the H2O-containing atmospheres.
著者
-
坂口 紀史
北海道大学エネルギー変換マテリアル研究センター
-
Sakaguchi Norihito
Laboratory Of Integrated Function Materials Center For Advanced Research Of Energy Conversion Materi
-
Sakaguchi Norihito
Laboratory Of Integrated Function Materials Center For Advanced Research Of Energy Conversion Materi
-
坂口 紀史
北海道大学
関連論文
- Microstructure and analysis of oxide scales formed on Cr-Si-Ni compacts in air and H2O-containing atmosphere
- イオン加速器連結型超高圧電子顕微鏡による金属間化合物創成プロセスのその場観察
- イオン注入を利用した対応粒界原子構造制御
- ファセット化したΣ3 CSL粒界原子構造のHRTEM観察と第一原理電子状態計算に基づく解析
- SUS301鋼におけるイオン注入によるマルテンサイト核形成
- 電子線照射下におけるTi/Cu界面微細組織のその場観察
- 電子線照射したFe-Cr-Ni合金における結晶粒界近傍での格子像と溶質偏析挙動
- 界面への高エネルギーイルミネーション
- 高効率エネルギー変換システム構築に向けた材料開発 : エネルギー変換マテリアル研究センターの紹介
- マルチビーム超高圧電子顕微鏡を用いた原子レベルでの界面構造評価
- In situ transmission electron microscopy observation of the decomposition of MgH2 nanofiber
- High-resolution electron microscopy of multi-wall carbon nanotubes in the subcutaneous tissue of rats
- Ion Implantation Induced Martensite Nucleation in SUS301 Steel
- Plane and Cross-Sectional TEM Observation to Clarify the Effect of Damage Region by Ion Implantation on Induced Phase Transformation in Austenitic 301 Stainless Steel
- Nano-scale phase transformation in Ti-implanted austenitic 301 stainless steel
- Radiation-induced segregation and precipitation behaviours around cascade clusters under electron irradiation
- EELS and Ab-Initio Study of Faceted CSL Boundary in Silicon
- Atomic Structure of Faceted *3 CSL Grain Boundary in Silicon : HRTEM and Ab-initio Calculation
- Influence of Silicon and Phosphorus on Radiation-Induced Segregation of Chromium and Nickel in Austenitic Model Alloys
- 235 フェーズフィールド法によるニッケル基合金のガンマプライム相発展シミュレーション(相転移・フェーズフィールド,塑性挙動のモデリングとシミュレーション-ナノからマクロまで-,オーガナイスドセッション5)