Flexural strength of the joint between glass-infiltrated alumina frames and the alumina-magnesia modifier.
スポンサーリンク
概要
- 論文の詳細を見る
PURPOSE: The purpose of the present study was to evaluate the flexural strength of the joint between glass-infiltrated alumina frames and the experimental adjusting agent (MA modifier) that contains alumina and magnesia. METHODS: A commercially available adjusting agent (Optimizer), a slurry of alumina powder (Alumina modifier), and a bulk specimen (joint-free alumina) were used as controls. Beam-shaped alumina specimens were machined from an alumina block. The ends of two alumina beams were positioned at an interval of 1.0mm and joined with each adjusting agent. The joined specimens were subjected to sintering, glass infiltration firing, glass control firing, and then a three-point bending test was carried out to evaluate the flexural strength. RESULTS: The maximum flexural strength was observed in the joint-free alumina, followed by MA modifier, Optimizer and Alumina modifier. With the exception for joint-free alumina, the failure modes after three-point bending test tended to shift from adhesive failure at substrate material-adjusting agent interface to cohesive failure within adjusting agent as the flexural strength increased. CONCLUSIONS: The use of MA modifier significantly improved the flexural strength of joined glass-infiltrated alumina frame. The MA modifier could be applied for adjusting the margin as an alternative to Optimizer when fabricating crown and bridge substructures with In-Ceram Alumina system.
論文 | ランダム
- Energetics and Occurrence Rate of Active-Region Transient Brightenings and Implications for the Heating of the Active-Region Corona
- High-Level Expression of the GLP-I Receptor Results in Receptor Desensitization
- 主観的な遮蔽表面と透明視がアモーダル表現の形成と仮現運動の対応問題の解決に及ぼす影響
- Conditions leading to flower formation on excised Begonia fragments cultured in vitro
- Othelloにおけるエリザベス朝心理学と芸術作品としての悪(日本英文学会第49回大会報告)