Transmission Electron Microscopy Observation of MgB2 Superconducting Materials with Inhomogeneous Microstructure: Influences of Specimen Preparation Methods
スポンサーリンク
概要
- 論文の詳細を見る
Transmission electron microscopy (TEM) observation of microstructure in MgB2 superconducting materials was carried out using different TEM specimen preparation methods. When a focused ion beam microsampling (FIB-MS) technique was applied to prepare thin foil specimens, TEM observation revealed inhomogeneous microstructure in MgB2 tapes fabricated by an in situ powder-in-tube (PIT) process: the microstructure composed of a densely crystallized MgB2 area, a partially crystallized area containing amorphous phases, micro-meter sized holes, etc. It was also revealed that doping with SiC in the PIT process makes distribution of the crystallized and partially crystallized areas uniform. On the other hand, when a conventional TEM specimen preparation, pulverizing the specimen into powders and thinning the powders with an Ar ion mill was performed, the microstructural characters of the MgB2 tapes described above were hardly recognized.
論文 | ランダム
- 203.口腔外科領域における下顎管断層について : 断層撮影-2
- 32.唾液腺造影撮影の一考察 : 東京部会 : 会員研究発表 : 頭部撮影
- Enhanced Enzymatic Reaction of Tyrosinase-immobilized Polyacrylamide-(γ-Cyclodextrin) Membrane Coated on a Platinum Disk Electrode in Acetonitrile
- In vitro proliferation and genetic diversity of Cypripedium macranthos var. rebunense
- Coherence Resonance in Propagating Spikes in the FitzHugh-Nagumo Model