Effect of Helium and Aging Treatment on Radiation Damage Behavior in Low Activation Fe-Cr-Mn (W, V) Alloy
スポンサーリンク
概要
- 論文の詳細を見る
Materials Science Forum, Volume 475-479The effects of helium and aging treatment on radiation damage behavior in low activation Fe-Cr-Mn ( W, V) alloy were investigated by electron and helium ion dual-beam irradiation in a high voltage electron microscope. Specimens were aged at 673 K, 823 K and 923 K for 1000, 3000 and 10000 hours. Electron and He ion dual-beam irradiations were performed at 627 K to 10 dpa. M23C6 type carbides were precipitated in the aged specimens, and the amount of the precipitates was increased with increasing aging temperature and aging time. He bubbles were formed during dual-beam irradiation in all of the specimens. The cavity swelling under dual-beam irradiations was increased with increasing the aging temperature and aging time. It was suggested that cavity swelling is closely related to the concentration of solutes such as Cr and C in the matrix, namely cavity growth rate becomes higher with decreasing of the solutes in solution.
- Trans Tech Publicationsの論文
Trans Tech Publications | 論文
- Photoinduced defects in CdS-doped glasses
- Oxidation behavior of Mo-Si-B in-situ Composites
- Solidification Behavior of Iron-Niobium and Iron-Carbon-Niobium alloys
- TDS Measurement of Hydrogen Released from Stainless Steel Oxidized in H2O-Containing Atmospheres
- Classification of Oxidation Behavior of Disilicides