The effect of La oxide additive on the solubility of NiO in molten carbonates
スポンサーリンク
概要
- 論文の詳細を見る
For practical use of molten carbonate fuel cells (MCFCs), Ni shorting due to NiO cathode dissolution during high-pressure operation is still a serious problem. The molten carbonate electrolyte should be more basic in order to reduce the NiO cathode solubility. In order to obtain a lower NiO solubility, the solubility of La oxide was investigated in the Li/Na/K and the Li/Na eutectic carbonates and the effect of the La oxide addition to the molten carbonate on the NiO solubility has also been investigated. The stable phase of La oxide in molten carbonate was found to be La2O2CO3 under P-CO2/P-O2 = 0.7/0.3 atm at 923 K. The solubility of NiO significantly decreased due to La additive in the acid dissolution region that is the operating condition for the MCFCs. The order of the base comparative index on the NiO solubility in the molten carbonate was La much greater than Ca = Sr > Li > Na > K. (C) 2004 Elsevier B.V. All rights reserved.
- Elsevier Science B.V.の論文
- 2005-02-02
著者
-
MITSUSHIMA Shigenori
Yokohama National University
-
Mitsushima Shigenori
Yokohama National University Graduate School Of Engineering
関連論文
- The Mechanism of Direct Formic Acid Fuel Cell Using Pd, Pt and Pt-Ru
- Catalytic Activity of Partially Oxidized Transition-metal Carbide-Nitride for Oxygen Reduction Reaction in Sulfuric Acid
- New Non-platinum Cathode Based on Chromium for PEFC
- Corrosion of Iron Coexisting with Molten Sodium Hydroxide and Sodium Peroxide
- Accelerated Corrosion of Stainless Steels with the Presence of Molten Carbonates below 923 K
- 水素エネルギーシステムと環境負荷係数
- Tantalum-based Compounds Prepared by Reactive Sputtering as a New Non-platinum Cathode for PEFC
- The effect of La oxide additive on the solubility of NiO in molten carbonates
- Exergy analysis of polymer electrolyte fuel cell systems using methanol
- Stability and electrocatalytic activity for oxygen reduction in WC plus Ta catalyst
- Solubilities of La and Ni on LaNiO_3 in Li/K Carbonate Eutectic with La_2O_3