GaAs- MISFETs with insulating gate films formed by direct oxidation and by oxinitridation of recessed GaAs surfaces
スポンサーリンク
概要
- 論文の詳細を見る
Direct oxidation by an ultraviolet (UV) and ozone process and oxinitridation (plasma nitridation after oxidation) of GaAs surfaces were used to form nanometer-scale gate insulating layers for depletion-type recessed gate GaAs-MISFETs. The drain current-drain voltage characteristics of the oxide gate devices exhibit lower transconductance (max. 40 mS/mm), lower breakdown voltage and smaller gate capacitance than the oxinitrided gate devices. The presence of hysteresis in the oxide gate devices is also apparent. The maximum transconductance of the oxinitrided gate devices is 110 mS/mm and they have a sharper pinch-off, compared to the oxide gate devices. In addition, no hysteresis is observed in their current voltage curves. The current gain cutoff frequency of 1.4 μm gate-length FETs for both types is 6 GHz. These results correspond well with results obtained from characterization of these insulating films.
- IEEEの論文
- 2004-03-00
IEEE | 論文
- Magnetic and Transport Properties of Nb/PdNi Bilayers
- Supersonic Ion Beam Driven by Permanent-Magnets-Induced Double Layer in an Expanding Plasma
- Surfactant Adsorption on Single-Crystal Silicon Surfaces in TMAH Solution: Orientation-Dependent Adsorption Detected by In Situ Infrared Spectroscopy
- Extended-range FMCW reflectometry using an optical loop with a frequency shifter
- Teachingless spray-painting of sculptured surface by an industrial robot