G030132 ECAPにより組織を微細化した銅の微小き裂進展機構([G03013]材料力学部門一般セッション(13):疲労とき裂)
スポンサーリンク
概要
- 論文の詳細を見る
Rotating bending fatigue tests were carried out on specimens of ultrafine grained copper produced by equal channel angular pressing. The growth behavior of a small surface-crack was monitored. A major crack, which led to the final fracture of the specimen, initiated from shear bands (SBs). After initiation, the crack grew linearly in the shear direction of the final pressing. A decrease in growth rate with a change in growth path morphology occurred when the crack length reached 1- 0.1 mm. This decrease occurred because of a change in the crack growth mechanism and is explained by considering the interrelation between grain size and the reversible plastic zone size at the crack tip.
- 一般社団法人日本機械学会の論文
- 2011-09-11
著者
-
横尾 勇治
大分大学大学院工学研究科
-
後藤 真宏
大分大学
-
Han Seung-zeon
Korea Institute of Materials Science
-
Kusno Kamil
大分大学大学院
-
Euh Kwengjun
Korea Institute of Materials Science
関連論文
- 629 超微細粒銅の長寿命域における疲労強度と表面損傷の形成挙動(超高サイクル・強度予測,疲労破壊の防止と評価,オーガナイスドセッション1)
- 617 インコネル718の超音波疲労(微視組織・き裂進展,疲労破壊の防止と評価,オーガナイスドセッション1)
- 130 Ni基超合金の中高温疲労強度に及ぼす結晶粒径の影響(微視組織と疲労強度評価VI, 疲労の実際と最新の話題 微視組織と疲労強度評価)
- 623 インコネル718の中高温疲労における内部破壊について(高サイクル疲労II,オーガナイズドセッション1.疲労の計測・解析・評価)
- 304 異方性を有する時効硬化Al合金の超音波疲労(ギガサイクル疲労,疲労における機構と評価,オーガナイスドセッション1)
- 518 切欠材の疲労強度に及ぼす結晶粒径の影響(炭素鋼の疲労強度,一般セッション)
- 313 時効処理された Cu-6Ni-2Mn-2Sn-2Al 合金の疲労挙動
- 113 S20C 焼なまし平滑材のき裂進展速度の変動
- 016 CU-2.5FE-0.1P合金の引張強さに及ぼす熱加工処理と微量の炭素添加の影響(GS2-2 一般セッション)
- OS3-11 超微細粒銅のき裂進展挙動に及ぼす応力レベルの影響(OS3-II 材料の性質評価)
- OS2606 銅合金CU-6NI-2SN-2MN-2ALのき裂発生および伝ぱ挙動に及ぼす微量のZR添加の影響(OS26-1 西谷弘信セッション1,OS-26 西谷弘信セッション)
- G030132 ECAPにより組織を微細化した銅の微小き裂進展機構([G03013]材料力学部門一般セッション(13):疲労とき裂)