Influence of the ultrasound (US) on the formation of hydrogen bonds in acrylic acid (AA) and N-isopropylacrylamide (NIPAM) polymer P(NIPAM-co-AA) was investigated. It was expected that the sonic wave led to change the breaking ability of the hydrogen bonds between AA and NIPAM under US exposure. The polymer solutions contained 4g P(NIPAM-co-AA) in 96ml water was used. In the polymer solution, viscosity was measured when B type viscosity meter was used with 6 and 60 rpm rotation after exposure of different frequency (28, 45, 100 kHz) and the power of US (200W). It was found that hydrogen bonds were broken by irradiating the US. As a result, the viscosity of the solution decreased and increased with and without the exposure of US
- 日本ソノケミストリー学会の論文
- 2009-10-23
著者
関連論文
- F-2 超音波場の制御による多孔質膜の透過効率向上(ソノケミストリー・強力超音波,口頭発表)
- 超音波膜処理プロセスの水浄化への応用 (特集 ソノテクノロジーの応用)
- PA-5 超音波を利用した膜水処理プロセス
- 超音波を利用した新しい膜水処理プロセス (特集 化学工学のフロンティア1999)
- 大腸菌懸濁液内でのANSの発光挙動
- マイクロ波放電により生成した励起一重項酸素流れにおけるハロゲン化銅の化学発光
- 荷電型限外濾過膜
- 荷電を有する限外濾過膜--荷電型限外濾過膜の特性と溶質透過
- マイクロ波放電流れ中の酸化窒素の分解による生成する窒素のCARSと紫外線可視領域の発光の観察
- 超音波-膜ハイブリッドプロセスでの超音波効果 (特集/ソノケミストリーの新しい進展)
- 分子インプリント膜のビスフェノールA吸着維持能の基礎的検討
- 超音波刺激応答特性を持つポリマーナノサイズゲル (特集 ソノケミストリーの最新動向(1))
- P17 超音波による不飽和脂肪酸およびそのエステル誘導体の乳化分散(ポスターセッション)
- P25 感温性ポリマーマイクロゲルの膨潤挙動における超音波照射効果
- P33 アルミナとポリアクリル酸の水素結合に対する超音波効果(ポスターセッション)
- A01 水溶性感温性ポリマーの水素結合形成に対する超音波効果
- P40 2,3-ジアミノナフタレンによる超音波媒体中で生成されるNO_2^-の定量及び評価(ポスターセッション)
- P20 高周波超音波照射による水エマルションの解濁効果(第II部,ポスター発表)
- P03 カラギーナンハイドロゲル物性に及ぼす超音波効果(ポスター発表)
- P21 超音波によるオゾン水の分解挙動(第I部,ポスター発表)
- P1 Coumarinプローブによる超音波場の評価(Poster Session)
- P21 均一液液抽出で形成されるイオン液体における超音波の影響(Poster Session)