4 シリコンアルコキシドのゾルゲルプロセスに対する超音波照射の影響
スポンサーリンク
概要
- 論文の詳細を見る
Sol-gel process in the ternary system of tetraethylorthosilicate (TEOS)-H_2O-ethanol was subjected to a power ultrasound of 20kHz-15W/cm^2. Sonication abruptly reduced the gelling time, and enhanced polycondensation to form Si-O-Si bonds. The ultrasonic effect increased with the increasing time up to 〜2 hours, and decreased with the increasing temperature. The latter is due to the "sonochemical effect" which prefers lower pressure of solvent vapor in the bubbles at lower temperature. On the other hand, argon-substituted atmospehre which should have higher effect of sonochemistry did have a lower effect than unsubstituted atmosphere (air). Comparing the sol-gel processes in N_2, O_2, Ar, and air, we found that oxygen has a positive effect on emulsification between TEOS and water. Ultrasonic-derived xerogels have higher density and specific surface area, and smaller pore size than normal ones. Incorporation of ammonia in the ternary causes the catalytic enhancement of polycondensation, resulting in the formation of spherical particles at a certain concentration condition. Ultrasonication to the system induced the polymerization at the surface of particles. The spherical shape was preserved when the particle size is as large as 300nm, while it was not when as small as 50nm. Ultrasonic effect on the sol-gel process might involve different mechanisms for homogeneous and heterogeneou systems.
- 日本ソノケミストリー学会の論文
著者
関連論文
- P14 磁性ナノ粒子のソノケミカルプロセス : 進行波場と定在波場の比較(物質創製、他)
- A21 無機ナノ粒子の湿式合成における出発溶液のエイジングとソフトソニケーション効果
- P16 粒径制御技術に対するソフトソニケーションの可能性(物質創製、他)
- 4 シリコンアルコキシドのゾルゲルプロセスに対する超音波照射の影響