GS03 CFRPの曲げクリープ特性と破壊じん性に及ぼす吸水及び凍結の影響(GS-1 一般セッション1,一般セッション)
スポンサーリンク
概要
- 論文の詳細を見る
Mechanical property of CFRP decreased by water absorption. In this study, effects of water absorption and freezing on flexural creep property and fracture toughness of CFRP are investigated. Water absorption test was conducted at 90℃ for 24, 48 and 72 hours. After water absorption, the specimens were kept in the -15℃ environment for 24 hours. The dimension of the specimen increased due to water absorption. The increase rate of thickness in freezing was bigger than that of only water absorption environment. Cracks occurred in the interface during water absorption. The interfacial crack progressed when the freeze expansion occurred. Therefore, creep property and fracture toughness of CFRP decreased. In addition, it is thought that creep properties decreased due to the decrease of a glass transition point after water absorption.
- 一般社団法人日本機械学会の論文
- 2011-07-16
著者
関連論文
- 平織り炭素繊維を用いたCFRPの曲げ特性に及ぼす表面処理の影響(S07-4 複合材料II,S07 メゾスケールにおける先進材料の力学と強度・機能評価)
- 平織り炭素繊維を用いたCFRPの層間破壊特性に及ぼす表面処理の影響(GS6 複合材の破壊)
- 224 炭素繊維強化複合材料の強度及びクリープ特性に及ぼす吸水の影響(複合材料I,一般セッション)
- 炭素繊維強化複合材料の曲げ強度及びクリープ特性に及ぼす吸水の影響
- 2118 ジュート繊維強化複合材料の引張り強度特性に及ぼす表面処理の影響(S23-3 グリーンコンポジットの機械的性質(2),天然繊維,リサイクル,S23 グリーンコンポジットの最前線)
- 519 CNBR 変性エポキシ母材を用いた CFRP の強度特性に及ぼす試験温度の影響
- CFRPの破壊及びクリープ特性に及ぼす物理的表面処理の影響
- エポキシ母材の架橋ゴム変性によるCFRPの静的, 衝撃および疲労特性の向上
- GFRPの疲労損傷過程に及ぼす希硫酸水溶液の影響
- サンドイッチ複合材料の曲げ特性に及ぼす表面材及び心材の影響
- ICCE/8(第8回複合材料工学の国際会議)に参加して
- 340 グリーンコンポジットの吸水及び熱疲労が静的強度特性に及ぼす影響(複合材料III,一般セッション)
- "Zhejiang Sci-Tech University and JCOM Joint Workshop on Composite Materials" and "Third China-Japan Joint Seminar on Green Composites"
- GS03 CFRPの曲げクリープ特性と破壊じん性に及ぼす吸水及び凍結の影響(GS-1 一般セッション1,一般セッション)
- GS04 ジュート繊維強化複合材料の引張りクリープ特性に及ぼす表面処理の影響(GS-1 一般セッション1,一般セッション)
- 一方向ジュート紡績糸強化生分解性プラスチックの疲労特性に及ぼすマトリックスの影響