ナトリウム四ケイ素雲母の膨潤特性とガスバリア能
スポンサーリンク
概要
- 論文の詳細を見る
Na tetrasilisic mica (Na-Ts) utilized as gas barrier filler was investigated in this study. It revealed that synthetic Na-Ts was actually composed an aggregation of some single crystals which have about 50nm thickness. They split to each particle once water is added. Also, aspect ratio (ratio of diameter to thickness) of dispersed Na-Ts in water is more than 3,600. Therefore, Na-Ts coated film brings out gas barrier ability most effectively among films including one. This is because Na-Ts particles are (1) not crushed, (2) concentrated in a certain narrow space of the film, (3) orientated well, when we select to coat Na-Ts on films.
- 2011-08-10
著者
関連論文
- P34 Na四ケイ素雲母のガスバリア性能(ポスター発表,一般講演)
- P21 マイカコートフィルムのガスバリアメカニズム(ポスター発表,一般講演)
- P56 Na四ケイ素雲母のアスペクト比
- P28 Na四ケイ素雲母の膨潤挙動(ポスター討論)
- P7 Na四珪素雲母の熔融合成における添加物と共成鉱物相
- マイカの合成とその応用(生活空間・身の回りの粘土 : 粘土圏環境における粘土の利用)
- ナトリウム四ケイ素雲母の膨潤特性とガスバリア能
- P51 Na 四珪素雲母懸濁液のアルコール凝集性
- P7 Na四珪素雲母の溶融合成における添加物と共成鉱物相
- P42 高アスペクト比/大粒子径ナノコンポジット用マイカ
- 合成マイカの用途展開
- 合成マイカとその応用(粘土基礎講座I : 粘土基礎講座Iワーキンググループ連載解説)
- A15 Li添加合成楊主明雲母(カリウム四ケイ素雲母)の結晶構造解析(口頭発表,一般講演)
- B10 カリウム四ケイ素フッ素雲母(K-TSFM)の結晶構造(第2報)(口頭発表,一般講演)