1105 計算熱力学を援用した鉄基多成分系合金のデンドライト組織予測(OS11.フェーズフィールド法とその応用(1),オーガナイズドセッション)

スポンサーリンク

概要

• 論文の詳細を見る

• Dendrite pattern in solidified alloys characterizes the solute segregation pattern and often result in the formation of second phases in the interdendritic region, which deteriorate the properties of materials. Hence, the evaluation of the complex dendrite pattern is quite important for controlling the solidified structure of an alloy. The complex dendrite pattern exhibits self-similar structure with spatial periodicity, i.e. the fractal structure. In the present study, a phase-field simulation was carried out for the formation of the dendrite pattern in Fe base multi-component alloys. The fractal dimension of the simulated dendrite patterns was calculated based on the box counting method. The complexities of dendrite patterns were evaluated by using fractal dimension, and the effect of the process variables such as solute element, cooling rate and composition on the dendrite pattern formation was examined.

• 一般社団法人日本機械学会の論文
• 2009-10-10

著者

• 伊藤 利久

  北大院

• 大笹 憲一

  秋田大

関連論文

• 1105 計算熱力学を援用した鉄基多成分系合金のデンドライト組織予測(OS11.フェーズフィールド法とその応用(1),オーガナイズドセッション)
• 235 フェーズフィールド法によるニッケル基合金のガンマプライム相発展シミュレーション(相転移・フェーズフィールド,塑性挙動のモデリングとシミュレーション-ナノからマクロまで-,オーガナイスドセッション5)
• 合金のデンドライト成長シミュレーション(デンドライトとウィスカ)

スポンサーリンク