S0301-3-6 Ni基単結晶超合金の疲労き裂進展挙動(疲労き裂進展と疲労強度)
スポンサーリンク
概要
- 論文の詳細を見る
The effect of crystallographic orientation on Fatigue crack growth behavior of single crystal superalloy CMSX-4 has been examined in the room temperature, 500℃, 700℃, and 900℃. Loading direction and initial crack direction were [001]・[010], [011]・[011^^-], and [111]・[112^^-] respectively. At room temperature crack growth occurred on the {111} octahedral slip planes at an oblique angle to the loading direction, while at high temperature crack growth occurred Mode I type failure process. Crack growth rate were discussed in terms of the effective stress intensity factor range which considers the effect of elastic anisotropy and inclined crack.
- 2009-09-12
著者
関連論文
- S0301-3-6 Ni基単結晶超合金の疲労き裂進展挙動(疲労き裂進展と疲労強度)
- 圧力機器の亀裂状欠陥評価方法HPIS Z101
- HPIS Z101第2段階評価における円筒表面欠陥の応力拡大係数評価法
- OS6-06 ガスタービン静翼の熱疲労き裂進展評価(OS6 設備診断・運用保全技術)
- 910 高中圧蒸気タービン内部車室の応力解析とき裂進展評価(OS-5 非定常熱弾性,非弾性,相変態,研究発表講演)
- ガスタービン動翼後縁冷却孔部のき裂進展評価(FP3 設備診断・運用技術2)
- 615 IN738LC の高温疲労き裂進展特性
- 807 ガスタービン耐食コーティングの割れ発生挙動
- 等間隔で平行な複数き裂の進展挙動に及ぼすき裂間隔の影響
- 723 有限要素法によるガスタービン静翼の熱応力解析(GS-3 実機,実物(2))
- 等間隔で平行な複数の片側切欠きを有する試験片の4点曲げ疲労き裂進展挙動
- 熱疲労下におけるガスタービン動翼の複数き裂進展挙動評価
- 等間隔で平行に導入された複数の片側切欠きからの疲労き裂進展試験(S10-2 実験,S10 熱応力と強度評価)
- (5)低圧タービンロータ翼溝部の腐食疲労き裂伝ぱ余寿命評価(日本機械学会賞〔2003年度(平成15年度)審査経過報告〕)
- 515 ガスタービン動翼の熱疲労下において交互選択的に成長する複数き裂の進展挙動評価
- 低圧タービンロータ翼溝部の腐食疲労き裂伝ぱ余寿命評価
- 622 長さの異なる複数の片側き裂を有する帯板の応力拡大係数
- 918 ガスタービン動翼の熱疲労下における複数き裂進展挙動評価
- 612 複数の片側き裂を有する帯板の応力拡大係数
- 701 片側き裂を有する帯板の応力拡大係数
- 456 低圧タービンロータ翼溝部における腐食疲労によるき裂進展方向の推定(GS-12 き裂(3))
- 低圧タービンロータ翼溝部の腐食疲労き裂伝ぱ余寿命評価
- 204 偏心引張圧縮疲労による複数き裂進展挙動(OS-1 疲労破壊の評価)
- 高中圧タービン翼溝部のクリープき裂伝播余寿命評価に関する取り組み