Fracture Mechanics Analysis on Structural Failure of Ships

スポンサーリンク

概要

• 論文の詳細を見る

• Structural failure of a bulk carrier equipped for carriage of vehicles was caused in gale sea under service condition of carrying vehicles enroute from Japan to Canada, where cracked damage was found at upper deck plate and slant plate of topside tank near the after corner of No.3 cargo hatchway port side. The failure analysis is made using the fracture mechanics on the phenomenon such as the fast fracture of upper deck plating and the fatigue crack initiation in upper deck as well as fatigue crack propagation and initiation in hatch end coaming bracket.

• 財団法人日本海事協会の論文

著者

• Tsutsui Yasuharu

  Research Institute Of Nippon Kaijikyokai

• Ikeda Hitoshi

  Classification Department Of Nippon Kaijikyokai

• Yasuda Kenji

  Classification Department Of Nippon Kaijikyokai

• Masuda Yoshiro

  Executive Vice President Of Nippon Kaijikyokai

• Ino Yukio

  Research Institute

• Ino Yukio

  Research Institute Of Nippon Kaijikyokai

関連論文

• Fracture Mechanics Analysis on Structural Failure of Ships
• 14. Fracture Mechanics Analysis on Structural Failure of Ships
• Failure analysis of propeller blade

スポンサーリンク