Tension-Torsion Multiaxial Creep-Fatigue Lifetime for CMSX-2 Nickel Base Single Crystal Superalloy

スポンサーリンク

概要

• 論文の詳細を見る

• In this paper, the tension-torsion multiaxial creep-fatigue lifetime for CMSX-2 nickel base single crystal superalloy at 1173K is described. Strain controlled tension-torsion low cycle fatigue tests with various hold times were carried out using hollow cylindrical specimens, the axis of which coincides with the [001] crystallographic direction. An introduction of the hold time into the torsion tests was more detrimental to the lifetime than that into the tension tests. The Von Mises' equivalent strain range gave a larger scatter for the correlation of creep-fatigue lifetimes. The relationship between elastic strain range and creep-fatigue lifetime had a strong dependency on the principal strain ratio. But those between plastic strain and the lifetime, and creep strain and the lifetime had almost no dependency on the principal strain ratio. A linear damage rule yielded an accurate lifetime estimation in the tension tests, but substantially overestimated the lifetimes in the torsion tests. A new simple lifetime prediction method, taking account of anisotropy of the elastic modulus, was proposed. The method predicted the experimental lifetime within a factor of 3 scatter band. Cracks in the tension tests propagated in the principal strain direction but those in the torsion tests propagated in the maximum shear direction. In the torsion tests, cracks were only observed in the soft zones predicted by numerical analyses.

• 社団法人日本材料学会の論文
• 2004-03-15

著者

• Sakane Masao

  Faculty Of Science And Engineering Ritsumeikan University

• HIYOSHI Noritake

  Department of Mechanical Engineering, Ishikawa National College of Technology

• Hiyoshi Noritake

  Department Of Mechanical Engineering Ishikawa National College Of Technology

関連論文

• Comparison of Local Strain at the Notch Root Between FEM Analysis and Experimental Strain Measurement Under Creep-Fatigue Conditions
• A Study of High Temperature Low Cycle Fatigue Criterion in Biaxial Stress State
• Tension-Torsion Multiaxial Creep-Fatigue Lifetime for CMSX-2 Nickel Base Single Crystal Superalloy
• Fatigue Crack Propagation for Cast Iron Rotating Disk
• Vibration of Nickel-Base Single Crystal and Directionally Solidified Superalloy Plates
• A Study on Creep-Fatigue Interaction of Polycrystalline Metal at Elevated Temperature : Specially, on the Effect of Hydrostatic Pressure on Crack Behavior.

スポンサーリンク