ポリウレタン : 構造と物性との相互関係
スポンサーリンク
概要
- 論文の詳細を見る
Aliphatic and aromatic polyurethanes were prepared from aliphatic and aromatic diisocyanates, such as hexamethylenediisocyanate (HDI) and 4,4'-diphenylmethanediisocyanate (MDI), and polyoles of ether and ester typies, such as polytetramethyleneglycol (PTMG) and polycaprolactam (PCL), by the prepolymer method, and then its physical properties, such as tensile test, swelling test, DSC and so on, were measured. These results were compared with the chemical structures calculated by MM2. Aliphatic and aromatic polyurethanes have with pseudo-helix-coil structure, and the structures of aliphatic polyurethanes were linear nearly and the structures of aromatic polyurethanes were alternate crossing structure. The physical properties of aliphatic and aromatic polyurethanes were correspondent with the structures calculated MM2 in expectation.
著者
関連論文
- ポリウレタン : 構造と物性との相互関係
- ノルボルナンジイソシアナートおよび水酸基末端ポリブタジエンより生成されるポリウレタンの平行光線透過率の温度依存性
- ノルボルナンジイソシアネートを用いたポリウレタンエラストマーの物性
- 各種シランカップリング剤によるガラス表面の改質
- AIT愛知工業大学 : 工学部応用化学科
- 脂環式ジイソシアナート : 銅アセチルアセトナート錯体触媒によるメタクリル酸メチルの重合
- 水ガラスを用いた複合化 : ケイ酸2-ビニルピリジニウム-スチレン-ブタジエン共重合体ゴムの調製および物性
- ジイソシアナート-遷移金属錯体触媒によるメタクリル酸メチルの重合
- 天然ゴムの構造変性による高減衰ゴム材料の開発
- ポリカプロラクトン系ポリウレタンの結晶性に及ぼす連鎖分布の影響
- ポリウレタン合成におけるアミン触媒の構造および物性への影響
- 緑茶の機能である抗菌・消臭性を付与したポリウレタンフォーム
- キュアラテックスを用いたラテックス共沈法によるブレンドゴムの調製とその物性
- ポリエステル系ポリウレタンエラストマーの電歪挙動
- 天然ゴムの構造変性による高減衰ゴム材料の開発
- 連鎖分布の規制されたPTMGから得られるポリウレタンの諸特性
- ポリウレタンエラストマーの電歪挙動
- 高結晶性オリゴユニットを構成単位とするエラストマーの合成と性質
- 高結晶性オリゴユニットを構成単位とする弾性高分子鎖の合成と性質
- 金属錯体を触媒に用いたポリウレタンのグリコリシス反応における酸の添加効果
- トリス(2-ヒドロキシエチル)イソシアヌレートの分解
- ポリウレタンのリサイクル
- 愛知工業大学の薬品管理体制の確立