雲母合成用坩堝の研究(第1報) : (合成雲母に關する研究 第XIX報)市販及び試作坩堝の耐蝕性
スポンサーリンク
概要
- 論文の詳細を見る
Several kinds of crucibles obtained from the market and special markers were tested for the corrosion on the synthetic phlogopite melt. High aluminous grog crucibles were attacked easily by the melt. The melt penetrated through pores of the wall and reacted with the soft bond and the perifery of the grog particles. A loose layer of spinel octahedrons was formed along the wall of crucible as the reacion product. The corundum crystals grew larger, when they contacted with the melt. These crucibles could not be used for a slow cooling experiment. Roseki(Agalmatolite) crucible was attacked from the surface. Spinel crystals produced were scattered in the melt. Small amount of forsterite needles and hexagonal skeleton crystals were formed, too. The latter were estimated to be cordierite crystals from their optical pro perties. Sintered corundum crucible stood to a heavy duty. Itwas attacked gradually from the surface. A reaction layer of spinel crystals and 'glass was formed along thewall. Many round pores were found in the layer. "Magnite" crucibles were prepared specially by KUROSAKI YOGYO K. K. from calcined dunite and magnesite. It was comoosed of forsterite crvsttals and a small amount of periclase, small particles of iron conpound, glassy matter and many pores. The melt penetrated through the wall and reacted with the matrix. The olivine crystals were not affected. Among the above mentioned crucibles, only the sintered corundum crucible can be used for a slow cooling experiment. Artificial graphite crucibles were used conveniently for the non-wetting property for the melt. But the carbon made the atmosphere to be reducing and accelerated the evaporation loss of the components of the melt The solidified mass was colored, light gray. Electro-plated chromium lining-prevented the reduction somewhat. Hard porcelain crucible was attacked largely, The solidified mass became very hard and difficult to split off mica crystals.
- 社団法人日本セラミックス協会の論文
- 1949-05-01
著者
関連論文
- 市販機器の透光度と微構造について
- 黒鉛化の速度過程に対する熱履歴の影響
- コバルト橄欖石(Co_2SiO_4)結晶の育成
- 特殊塩基性耐火物の研究
- 蛍光 X 線スペクトルによるガーネット中の Al の配位状態の安定
- 合成雲母の育成
- 「人工鉱物の現在と将来」
- 故型石膏の再生
- 高温高圧下におけるCo3Al2Si3O12-Y3Al5O12系の柘榴石の反応生成領域
- Co3Al2(SiO4)3-Y3Al2(AlO4)3系の生成鉱物
- コバルト柘榴石(CO3Al2Si3O12)の高圧合成とその安定領域
- 3CoO・Al2O3・3SiO2-3Y2O3・5Al2O3系の相平衡
- 人工鉱物に関する座談会
- 市販磁器の透光度と微構造について
- 合成雲母結晶製造実験用炭素粒抵抗電気炉の設計と性能
- 磁器の透光度におよぼす滑石添加の影響-2-
- 磁器の透光度におよぼす滑石添加の影響-1-
- 磁器焼成過程における炭素の沈析と磁器の色調-粘土の種類を変えた場合の影響-
- サイプラス島産石膏よりの焼石膏の熟成-2-
- 磁器中の微量炭素の定量法-乾式法と湿式法との比較-
- サィプラス島産石膏よりの焼石膏の熟成
- 合成雲母結晶製造実験用炭素粒抵抗電気炉の設計と性能 : 合成雲母に関する研究所, 第XXXVI報
- 私と結晶成長
- 結晶づくりむかし話 : 人工鉱物討論会前史
- 高温高圧下における Co_3Al_2Si_3O_-Y_3Al_5O_ 系の柘榴石の反応生成領域
- 3CoO・Al_2O_3・3SiO_2-3Y_2O_3・5Al_2O_3 系の相平衡
- Co_3Al_2(SiO_4)_3-Y_3Al_2(AlO_4)_3系の生成鉱物
- コバルト柘榴石(Co_3Al_2SiO_3O_)の高圧合成とその安定領域
- 石英ガラスによるスクイザー型高圧装置圧力室内の圧力分布の測定
- 珪酸ガラスの屈折率の圧力依存症を利用した高圧装置中の圧力分布測定
- 合成石膏の研究
- 雲母合成用坩堝の研究(第1報) : (合成雲母に關する研究 第XIX報)市販及び試作坩堝の耐蝕性
- フッ素金雲母結晶の育成
- サイプラス島産石膏よりの燒石膏の熟成 (第1報)
- サイプラス島産石膏よりの焼石膏の熟成 (第2報)
- 磁器の透光度におよぼす滑石添加の影響 (第2報) : 磁器の色調と第1鉄対第2鉄比
- 磁器焼成過程における炭素の沈析と磁器の色調粘土の種類を変えた場合の影響
- 磁器中の微量炭素の定量法乾式法と湿式法との比較
- 蛍光X線分析用分光結晶の熱膨脹と温度制御