E-2 TENSION-TORSION CREEP FRACTURE BEHAVIORS OF NOTCHED SPECIMENS OF AUSTENITIC STEEL SUS310S(Session: Thermal Fatique/Creep)
スポンサーリンク
概要
- 論文の詳細を見る
Using notched specimens of austenitic steel SUS310S, creep rupture tests are conducted in tension, torsion and combined tension-torsion stress states at 700℃. The creep fractures especially the initiation and growth behaviors of creep voids in the specimens are investigated and discussed. It is suggested that the von Mises effective stress and the mean stress promote the initiation and growth of creep voids, respectively.
- 一般社団法人日本機械学会の論文
- 2006-11-08
著者
関連論文
- Hot Water Jet Erosion Characteristics of Ti-Ni Shape Memory Alloys
- Tensile Fracture Behaviors in Double-notched Thin Plates of a Ductile Steel
- Initiation and Growth Behavior of Creep Voids in an Austenitic Steel with High Ductility under Multi-axial Stresses
- Creep Rupture Properties of an Austenitic Steel with High Ductility under Multi-axial Stresses
- Effect of Stress States on Creep Fracture Modes of an Austentic Steel with High Ductility
- E-2 TENSION-TORSION CREEP FRACTURE BEHAVIORS OF NOTCHED SPECIMENS OF AUSTENITIC STEEL SUS310S(Session: Thermal Fatique/Creep)
- Accelerated Corrosion Behavior due to Alternating Dry-Wet Conditions for LP Steam Turbine Materials of Fossil Power Plants
- Tension-Torsion Creep Fracture Behaviors of Notched Specimens of Austenitic Steel SUS310S