B-2 SURFACE COATING FOR DUCTILE CAST IRON BY CONSOLIDATION AT LOW HEAT IN MECANICALLY ALLOYED Ni-Al-Si POWDERS(Session: Coatings)
スポンサーリンク
概要
- 論文の詳細を見る
Mechanical alloying (MA) of Ni-74.9mol%Al-3.1mol% Si powder mixtures was performed for relatively short milling times by planetary ball mill. The MA powders were coated on ductile cast iron (JIS-FCD450) by vacuum hot pressing at a relatively low temperature (873K) to investigate potential for mechanochemical activation of MA on surface coating. At the optimal milling time, the coated layer was well-reacted with high density (almost no pores) and high hardness (max. 1110HV).
- 一般社団法人日本機械学会の論文
- 2006-11-08
著者
-
Okabe Takuji
Department Of Mechanical Systems Engineering Faculty Of Engineering Hiroshima Institute Of Technolog
-
Okabe Takuji
Department Of Mechanical Systems Engineering Faculty Of Engineering Hiroshima Institute Of Technolog
関連論文
- B-2 SURFACE COATING FOR DUCTILE CAST IRON BY CONSOLIDATION AT LOW HEAT IN MECANICALLY ALLOYED Ni-Al-Si POWDERS(Session: Coatings)
- Consolidation at Low Heat in Mechanically Alloyed Ti-Al Powders(Recent Advances in Materials and Processing (I))
- Adhesion of Atmospheric Micro-Contaminants on SUS304 Steel and Removal by UV Illumination