3918 作用応力推定のための疲労破面解析法の検討(S17-3 強度・変形・ひずみ評価,S17 実験力学における最近の展開)
スポンサーリンク
概要
- 論文の詳細を見る
Estimation of the applied stress to the fractured component is important in failure analysis in fatigue fracture accident in order to determine the cause of fracture and to prevent another failure. The estimation using striation spacing achieved success in the very limited range of ΔK. The objective of this study is development of estimation methods, which are applicable in the wide range of ΔK from crack propagation threshold to striation formation. Electric impedance method and fracture surface hardness one were examined. Electric impedance of fatigue fracture surface was measured within the plastic deformation layer by using high frequency current. The impedance increased with increase of the K value. Micro Vickers hardness was measured on the fatigue fracture surface. The hardness was defined as the area of indentation mark to reduce the effect of the roughness of fracture surface. The hardness increased with increase of the K value.
- 社団法人日本機械学会の論文
- 2006-09-15
著者
-
久保田 祐信
九州大学大学院工学研究院
-
近藤 良之
九州大学大学院工学研究院
-
久保田 祐信
九大工
-
近藤 良之
九大工
-
栄 中
九大工
-
小川 琢矢
九大院
-
栄 中
九州大学大学院工学研究院
-
小川 琢矢
九州大学大学院:(現)(株)東芝
関連論文
- 低合金鋼の下限界近傍の微小疲労き裂進展に及ぼす水素侵入と水素雰囲気の影響
- 低合金鋼の水素誘起き裂進展加速とき裂の開口状態について
- 低合金鋼SCM440Hの長周期変動応力下の水素誘起き裂進展加速に及ぼす水素濃度,板厚,周波数および温度の影響
- SUS304の水素ガス中フレッティング疲労における疲労限度低下機構
- ストライエーションが観察されないステンレス鋼疲労破面の微小硬さによる作用応力推定の試み
- 疲労限度以下の応力による2段2重変動応力下の疲労破壊に及ぼす微小切欠きの形状と水素の影響
- SUS304のフレッティング疲労強度に及ぼす水素雰囲気の影響(材料力学(転がり・摩擦・摩耗))
- SCM435H及びSUH660のフレッティング疲労特性に及ぼす水素ガス環境の影響(水素エネルギーシステムに使用される材料の強度問題)
- 402 フレッティング疲労標準試験法の問題点
- 低合金鋼SCM440Hの長周期変動応力下の水素誘起き裂進展加速に及ぼす水素濃度,板厚,周波数および温度の影響