3321 焼結合金WC-Coの長寿命疲労破壊機構(G03-1 衝撃・動的挙動,G03 材料力学)
スポンサーリンク
概要
- 論文の詳細を見る
Rotating fatigue test was carried out using the sintering WC-Co in ultra-long life. A sintered alloy has much defects on the boundary. A crack initiates from these defect, and propagates belong the boundary. Fatigue limit does not exist. Because the sintered alloy like ceramics obeys to weakest link. The boundary slips easily, and is weak to sharing force. The fatigue crack propagation rate (da/dN) cannot calculates. But, fracture toughness K_<IC> can calculate from relationship Fractal dimension or Hurst number and yield area. Yield area of fracture in ultralong N_f=2.05×10^7 broad. Origin of fracture is surface defect s. When K_<IC>>K_<max> in surface stands up, the crack in the plane stress propagate. The fatigue strength of WC cemented carbide is obeyed to weakest link model of defects. Because, even if it supposes that it was worked the cyclic stress over the fatigue strength, the fatigue fracture did not always happen.
- 一般社団法人日本機械学会の論文
- 2006-09-15
著者
関連論文
- アルミニウム合金の高速切削における工具材種の影響
- セラミック硬質被膜の弾性定数と残留応力に関する研究(X 線材料強度)
- 1011 複合表面改質を施した高速度工具網の疲労安全性保証(オーガナイズドセッション : 表面改質材の機械的安全性保証)
- 723 表面改質球状黒鉛鋳鉄の疲労強度信頼性評価
- 928 イオン浸炭処理 PDI 材の 2 段折れ曲がり
- 637 イオン浸炭処理切欠き PDI 材の疲労強度特性
- DLCと種々のTi系薄膜のフラクタル特性(GS8 マイクロ/ナノ試験・薄膜)
- K-0715 スーパ表面改質材の疲労信頼性に関するフラクトグラフィ的研究(S07-4 疲労信頼性の向上(薄膜,窒化))(S07 表面改質とその機能特性評価)
- 切削工具用コーティング膜の進歩(最先端薄膜技術)
- 108 イオン浸炭PDI材における疲労破面のメゾ組織(O.S.1-2 疲労特性II)(O.S.1 材料の変形・損傷・破壊の解析と評価)
- 708 焼結合金WC-Coの破壊じん性評価(変形・強度,一般セッション)
- 3321 焼結合金WC-Coの長寿命疲労破壊機構(G03-1 衝撃・動的挙動,G03 材料力学)
- 1322 ADIを用いた長寿命疲労破面のフラクタル次元解析(S21-2 疲労破面性状と疲労微視組織の解析,S21 金属材料の疲労特性と破壊機構)
- 127 共焦点型走査レーザー顕微鏡による疲労破面のフラクタル次元解析(微視組織と疲労強度評価V, 疲労の実際と最新の話題 微視組織と疲労強度評価)
- 薄膜打痕表面のレーザー顕微鏡観察とフラクタル次元解析(GS8 マイクロ/ナノ試験・薄膜)
- 427 損傷面の 3 次元フラクタル解析