水溶液中におけるSnO_2:F電極のナノTiO_2コーティング(<特集>水溶液科学に立脚したセラミックス合成プロセス)

スポンサーリンク

概要

• 論文の詳細を見る

• We produced a nano TiO_2 coating on SnO_2: F (FTO) electrodes in an aqueous solution. Anatase TiO_2 crystallized in the transparent solution at 50℃ for 10 min. The FTO electrodes with markedly uneven surface were successfully covered by nano TiO_2 without annealing. The TiO_2 was deposited on the electrodes with no clearance, thus attaining high adhesion strength. The coating showed high transparency, over 75%, in visible-light regions of 400 to 800 nm, which is similar to bare FTO electrodes. The electrodes had a unique surface structure resulting from the combination of uneven FTO surface and microasperity due to the nano TiO_2 coating.

• 社団法人日本セラミックス協会の論文
• 2007-12-01

著者

• 加藤 一実

  National Institute Of Advanced Industrial Science And Technology (aist)

• 増田 佳丈

  National Institute of Advanced Industrial Science and Technology (AIST)

関連論文

• 水溶液中におけるSnO_2:F電極のナノTiO_2コーティング(水溶液科学に立脚したセラミックス合成プロセス)
• セラミックスの液相パターニング(第60回日本セラミックス協会進歩賞受賞に関する総説及び論文)

スポンサーリンク