シリコン粉末の熱プラズマ炭化反応によって生成したコア・シェル構造Si-SiC複合粒子(秋季シンポジウム若手研究者論文)

スポンサーリンク

概要

• 論文の詳細を見る

• Unique core-shell-structured micron spheres of Si-SiC consisting of a layer of silicon carbide nanocrystallites and a silicon single-crystal core were synthesized by thermal plasma in-flight carburization of silicon micron powders in Ar-H_2-CH_4 plasma. Raman spectroscopy and energy dispersive X-ray spectroscopy (EDX) revealed the formation of silicon carbide particles on the surface of Si particles, and transmission electronic microscopy (TEM) showed a uniform distribution of SiC nano-sized grains (〜80nm) at a depth of 500nm beneath the surface of the composite spheres. Micron voids and nano pores were observed at the SiC-Si interface and in the Si matrix. The formation of long and thick SiC nanotubes was observed in the Si matrix near the SiC-Si interface. The mechanism of carburization reactions and the growth of silicon carbide layers and SiC nanotubes are discussed.

• 社団法人日本セラミックス協会の論文
• 2007-11-01

著者

• 石垣 隆正

  Nano Ceramics Center National Institute For Materials Sciences

• 李 亜利

  Nano Ceramics Center, National Institute for Materials Sciences

• 李 亜利

  Nano Ceramics Center National Institute For Materials Sciences:school Of Materials Science And Engin

関連論文

• 熱プラズマ中で蒸発したTiCとAlの凝縮反応によるTi_2AlCナノ結晶の生成
• シリコン粉末の熱プラズマ炭化反応によって生成したコア・シェル構造Si-SiC複合粒子(秋季シンポジウム若手研究者論文)
• 反応性熱プラズマを用いた無機材料合成
• 熱プラズマプロセッシングによる無機材料のナノ構造制御
• 低圧高密度プラズマプロセスによるナノクリスタルダイヤモンドコーティング (特集 コーティング技術--ナノテクを含む高機能化の最前線)

スポンサーリンク