車輪及びレール鋼における混合モード負荷による疲労き裂成長(力学特性)
スポンサーリンク
概要
- 論文の詳細を見る
Fatigue crack growth under mixed mode loading is an important problem in railway fields. Therefore, a method was developed and prepared to observe the fatigue crack propagation under mixed loading of tensile and in-plane shear modes by an in-plane biaxial fatigue machine. In the experiments, sequential and overlapping mode I and mode II cycles were applied to the crack in the cruciform specimen made of wheel or rail steel. Growth rate laws for wheel and rail steel were obtained by means of least square regression analysis in terms of both the effective stress intensity factor ranges. The fracture surfaces near the crack tip region of tested specimens were observed by SEM and dis- cussed to relate the superiority of pearlite structure over tempered martensite structure in detail.
- 2007-09-01
著者
関連論文
- メッシュフリー境界節点法による三次元表面き裂のK値解析
- 圧縮残留応力下での疲労き裂進展挙動
- 人工きず入り新幹線電車車軸の疲労試験結果に対する破壊力学的評価
- ショートクラック進展と摩耗の競合に関する数値シミュレーション
- 車輪及びレール鋼における混合モード負荷による疲労き裂成長(力学特性)
- 有限要素法による鋼ガス圧接時及び熱間せん断時の変形と応力の解析 : 鋼ガス圧接部ふくらみの熱間せん断による非破壊検査(第3報)
- 鉄道用低応力・低騒音軽量車輪の開発
- レール鋼の繰返し打撃による塑性変形挙動
- 人工きず入り新幹線電車車軸の疲労試験結果に対する破壊力学的評価 : 第2報, 中ぐり車軸の場合
- 確率論的破壊力学を用いた新幹線車軸の健全性評価
- 確率論的破壊力学を用いた新幹線車軸の健全性評価
- 境界要素法によるころがり-すべり接触場における混合モード表面き裂のK値解析
- 計算破壊力学による転がり接触疲労き裂のK値解析
- 1104 混合モードI及びIII負荷による疲労き裂成長に及ぼす材質と応力比の影響(OS11-1 材料の疲労挙動と損傷評価-き裂進展-)