積層複合材の板厚方向の衝撃圧縮特性(<特集>衝撃)
スポンサーリンク
概要
- 論文の詳細を見る
Through-thickness compressive characteristics of laminated composites at high rates of strain are evaluated using the standard split Hopkinson pressure bar. Three types of laminated composites, namely symmetric cross-ply carbon/epoxy, plain-woven carbon/epoxy and plain-woven E-glass/epoxy with almost the same thickness are tested at room temperature. Cylindrical compression specimens are machined such that the longitudinal direction of each specimen is parallel to the thickness direction of the laminates. The effects of strain rate, type of reinforcing fiber and prepreg form on the secant modulus, ultimate compressive strength, ultimate compressive strain and absorbed energy are examined in detail. It is shown that the cross-ply carbon/epoxy laminated composite exhibits the highest strength characteristics at low and high rates of strain, and there is no correlation between the absorbed energies and the Charpy impact energies for the laminated composites tested.
- 社団法人日本材料学会の論文
- 2004-03-15
著者
関連論文
- 粘弾性ホプキンソン棒法の低インピーダンス材料への応用
- 純マグネシウム押出し材の衝撃引張・圧縮特性
- ゴルフクラブヘッドのフェース面の板厚分布最適化(ゴルフ(1))
- 弾性的に結合されたチモシェンコ二重はり系の非定常振動
- ホプキンソン棒法による材料の衝撃変形強度の評価
- 高分子材料の衝撃圧縮応力-ひずみループの決定--円柱状試験片の細長比および潤滑剤の影響 ([日本実験力学会]2010年度年次講演会)
- 118 ゴルフボールの粘弾性モデルの決定(セッション5)
- ゴルフボールの粘弾性特性の評価(ゴルフ(1))
- 409 6061Al 合金摩擦圧接継手の衝撃引張特性
- 6061アルミニウム合金/SUS304ステンレス鋼摩擦圧接継手の衝撃引張特性