鋳片表層組織制御による圧延鋼片の表面疵防止(鋳造・凝固)
スポンサーリンク
概要
- 論文の詳細を見る
This study was carried out in order to make clear the crack generation mechanism of case-hardening steels. It was suggested from the average oxide particle radius around surface cracks of the rolled billets that most of the surface cracks should be generated at the bloom rolling process. From the point of view of surface crack generation at the rolling process, austenite grain sizes just before rolling were pointed out. In general, in order to prevent surface cracks at the rolling process, bainite or ferite/bainite structure before reheating is suitable for fine grain structure just before rolling. In order to get these structures, the cooling rate of the bloom surface should be higher than 2.0K/S under the cooling start temperature of 1023-1173K. It was proved that refining austenite grain in the bloom surface just before rolling was effective to decrease the crack generation.
- 2007-04-01
著者
関連論文
- 鋳片表層組織制御による圧延鋼片の表面疵防止(鋳造・凝固)
- 鋼材表面疵近傍におけるサブスケール層内の粒状酸化物の生成機構
- 鉛含有はだ焼鋼鋳片の表面疵改善(鋳造・凝固)
- はだ焼鋼の表面疵改善
- 高アルミニウム合金鋼の鋳片表面欠陥改善
- 鉛鋼鋳片の表面疵改善
- 粒状酸化物による表面疵発生温度域の推定