809 遮熱コーティング界面の酸化層成長解析 : 界面形状の影響と損傷メカニズムの検討(OS-8B,OS-8 界面と接着・接合の力学)

概要

論文の詳細を見る
Thermally grown oxide (TGO) layer is grown at the interface between top coating and bond coating when a coating system with thermal barrier coating (top coating) and both coaling is heated. The growth of the TGO layer causes the delamination of top coating from bond coating after heating. The growth of TGO layer had simulated by using finite element analysis model of the interface between top coating and bond coating and it depended on both the geometry of the interface and the temperature at interface in previous paper. In this paper, the fracture mechanism of TBC was examined from the observation at the interface after thermal cycle test. It was found that a lot of cracks were occurred in top coating near convexity of the interface when TGO layer was grown. The location of the occurrence of those cracks coincided with the simulation results.