高純度鉄の繰返し応力下における転位組織の観察

スポンサーリンク

概要

• 論文の詳細を見る

• Abstract　An investigation has been made by transmission electron microscopy of high-purity iron (99.996 at.%6) fatigued in reverse plane bending with zero mean stress. A thin foil preparation technique has been used that allows the same areas as those for optical micrography to be examined. It is shown that the distribution of dislocations at the surface is similar to the aspects of slip bands observed optically. Dislocation structures induced in high-purity iron by cyclic stressing over a range of stress amplitudes consist of jogged dislocations, dislocation loops, dislocation patches and subgrain structures. The most characteristic feature of the dislocation structures in low stress fatigue is the presence of large numbers of tiny loops.　概要　　繰返し曲げ応力を与え疲労させた高純度鉄（99.996 at.%）の疲労変形機構を追究するために，光学顕微鏡と同一視野の中から実物薄膜を作製し，特に試験片表面層（＜5μ）の転位組織を透過電子顕微鏡により直接観察した。表面層における転位分布の形態は光学的に観察されるすべり線の様相と類似している。また,繰返し応力を受けた高純度鉄の表面層に観察される転位組織はjogを有する転位，転位環，転位patchesおよびsubgrain組織等から構成される。特に，低応力疲労の特徴は小さい転位環が多数観察されることである。

• 山形大学の論文
• 1970-03-25

著者

• 菅野 幹男

  工学部共通講座

関連論文

• 結晶学的破面解析によるチタニウム薄板材の疲労き裂伝ぱ機構の検討
• 線引き加工したFe-Ni合金線における磁性および弾性の熱処理効果
• Fe-Si系合金の規則-不規則変態
• 高純度鉄の繰返し応力下における転位組織の観察

スポンサーリンク