塩化物を含む防水剤および表面活性剤の鉄筋の発せい(錆)に関する研究
スポンサーリンク
概要
- 論文の詳細を見る
(1) The objective of the study: Consequent upon the study of reinforced concrete using sea sand containing salt in fine aggregate, this study aims at investigating the influences on the corrosion of steel bars due to water-profing agents and surface-active agents containg salt, and obtaining informations on determining their suitability. (2) The method of the study: Firstly the content of Cl due to CaCl_2 or others, and pH of water-proofing agents and surface-active agents on the market were investigated. In the case of those acidic and containing Cl, the corrosion of bars was tested in the solution saturated with calcium hydroxide containing these admixtures by means of surveying the changing process of natural electrode potential. (3) Conclusion: (a) Among twenty four water-proofing agents on the market, four were found unsuitable to the use for reinforced concrete. These four contained Cl, one of then being acid and the others alkaline, but these all showed strong alkality in the solution saturated with calcium hydroxide. Nineteen others were not or very rare containing Cl, and found suitable to the use for reinforced concrete. (b) Among twenty seven surface-active agents, six were acid and seven containing Cl, but these all showed strong alkality in the solution saturated with calcium hydroxide. Though five of them contained especially greater quantity of Cl, they were all found not conducive to the corrosion of bars. This result, despite these greater content of Cl, shall be ascribable to the fact that these have some characteristics such as corrosion inhibitor. But one of seven contained Cl was found unsuitable to the use for reinforced concrete. This shall be caused by nothing of some characteristics like corrosion inhibitor. (c) I recomend that some water-proofing agents and surface-active agents having greater content of Cl should be admixed with corrosion inhibitor such as K_2CrO_4 or NaNO_2.
- 社団法人日本建築学会の論文
著者
関連論文
- 特殊骨材を用いるコンクリートの仕様に関する研究
- 1034 塩化物を含む防水剤および表面活性剤の鉄筋の発せい(錆)に関する研究(材料・施工)
- 塩化物を含む防水剤および表面活性剤の鉄筋の発せい(錆)に関する研究
- 1057 市販防水剤および表面活性剤を用いた場合の鉄筋の発せい(錆)について(材料・施工)
- 1048 三鷹航空技術研究所計測室プレストレストコンクリート工事報告(材料・施工)
- 1053 三鷹航空技術研究所せん音速風洞上家プレストレストコンクリート架構について : その2(応力導入測定について)(材料・施工)
- 1052 三鷹航空技術研究所せん音速風洞上家プレストレストコンクリート架構について その1 : その1 施工概要について(材料・施工)
- 22. 高さ80Mの落下傘塔の設計について(その2) : 基礎構造の設計について
- 21. 高さ80Mの落下傘塔の設計について その1 : 上部構造について
- 1024 鉄骨鉄筋砕石および軽石コンクリートの材料施工法に関する研究 : 主として付着における鉄筋とコンクリートの相対変位について(材料・施工)
- 119 鉄骨鉄筋砕石及び軽石コンクリートの材料施工法に関する研究 : 主として,鉄筋継手重ね長さと定着について(材料・施工)
- 2.鉄骨鉄筋砕石コンクリートの材料施工法に関する研究 : 主として砕石の粒形の良劣と調合補正について
- 1.鉄筋コンクリート用骨材としての海砂の利用に関する研究
- 104 鉄筋コンクリート用骨材として海岸砂の使用について