Comparative Studies on the Synthesis of Na-magadiite, Na-kenyaite and RUB-18 Phases(Synthesis of Clays,Proceedings of the 13^<th> International Clay Conference)

スポンサーリンク

概要

• 論文の詳細を見る

• Ludox-AS40, Colloidal silica, Ludox HS-40 and Fumed silica were used as silica sources, in order to prepare well crystalline Na-magadiite and Na-kenyaite layered silicates. The influence of reaction times, NaOH concentration and water contents in the mixture gel were investigated. Pure Na-magadiite phase was obtained after a hydrothermal treatment of Na_2O/5SiO_2/122H_2O gel, at temperatures below 150℃ for a period of 2 days reaction, independently of the silica source. However, better crystallinity was achieved using Ludox AS-40. Pure Na-kenyaite was formed only from Fumed silica at 170℃ and after 2 days of reaction. The water content affected the type of layered silicates when fumed silica was used. Indeed, pure Na-kenyaite was obtained at 150℃ and after 2 days of reaction using a gel of Na_2O/5SiO_2/24H_2O. Meanwhile, Na-magadiite was formed for a content of water above 70. A minimum content of NaOH (0.25Na_2O) was required to obtain Na-magadiite from Fumed silica and colloidal silica. The control of the transformation rate of Na-magadiite to Na-kenyaite or vice versa can be achieved by increasing the synthesis temperatures, or the gel compositions. We were able to block the transformation of Na-magadiite to Na-kenyaite by adding an organic solvent dioxane, and pure RUB-18 phase was obtained at temperatures above 130℃ after 1 day of reaction.

• 日本粘土学会の論文

著者

• Kooli Fethi

  Institute Of Chemical And Engineering Sciences

• Kooli Fethi

  Institute Of Chemicals And Engineering Sciences

• LI MIANHUI

  Institute of Chemicals and Engineering Sciences

• PLEVERT JACQUES

  School of Materials Science & Engineering

• Plevert Jacques

  School Of Materials Science & Engineering

関連論文

• Effect of Hexadecyltrimethylammonium (C16TMA) Counterions on the Intercalation Properties of Different Montmorillonites(Clay-Organic Intercalation Compounds,Proceedings of the 13^ International Clay Conference)
• Zirconium Nitrate Solution as Pillaring Agent of Montmorillonite Clays(Activated Clays and Porous Materials,Proceedings of the 13^ International Clay Conference)
• Porous Clay Heterostructures from Al_ Intercalated Montmorillonites : Synthesis and Characterization(Activated Clays and Porous Materials,Proceedings of the 13^ International Clay Conference)
• Comparative Studies on the Synthesis of Na-magadiite, Na-kenyaite and RUB-18 Phases(Synthesis of Clays,Proceedings of the 13^ International Clay Conference)

スポンサーリンク