銅を溶侵した焼結鋼の摩耗特性
スポンサーリンク
概要
- 論文の詳細を見る
The wear resistance of the powder sintered steel of having infiltrated the copper which melted after sintering has been investigated. The copper infiltrated-sintered steels set up some densities of the as-sintered material (i.e., base material), and was created. In the sintered steel whose defect was completely lost by copper infiltration, the abrasion loss decreases with the decrease in density of a base material (i.e., the increase in amount of infiltrated). The abrasion loss was changed by surface plastic processing, and use of the wear test partner material from which surface hardness differs. Formation of the oxide film in the friction surface decreased abrasion loss remarkably.
- 苫小牧工業高等専門学校の論文
- 2006-03-31
著者
関連論文
- ブレーキキャリパ用高強度・高靭性アルミニウム合金鋳物の引張りおよび疲労特性
- 純銅製配電用部品の摩擦圧接部の健全性と接合強度
- 高速摩擦加工による鉄鋼材料の表面改質強化
- 鋳鋼の疲労特性に及ぼす過大荷重の影響
- 銅を溶侵した焼結鋼の摩耗特性
- 軟鋼アーク溶接部の引張特性に及ぼす大気中湿度の影響
- アルミニウム合金鋳造材の機械的性質に及ぼす熱間圧縮加工の効果
- 軟鋼アーク溶接部の曲げ試験結果に及ぼす経過時間の影響
- 鋳鋼の水素脆性および遅れ破壊に及ぼす微小凝固欠陥の影響
- アルミニウム合金鋳物の引張り特性に及ぼすデンドライト組織と凝固欠陥の影響
- 高速摩擦加工による鉄鋼材料の疲労強度の向上
- オーステナイト系ステンレス鋼の表面塑性加工と漸増応力による疲労強度の向上
- 鋳鋼の疲労特性に及ぼす微小凝固欠陥の影響
- 鋳鋼の低サイクル疲労特性に及ぼす微小凝固欠陥の影響
- アルミニウム合金の拡散接合強度に及ぼす接合面間摺動の効果
- 22.3 技術史, 技術史教育(22.技術と社会)
- 函館地区における海洋関連機械工業の発展と産業遺産としての工作機械群
- 機械系の材料学と材料選定(随想・留学記・旅行記等)(支部だより)
- 中炭素鋼連続鋳造材の引張り破断特性に及ぼすデンドライト分離欠陥の影響
- 密度の異なる焼結鋼の機械的性質と被切削性の改善に及ぼす銅溶浸の効果
- 銅溶浸焼結鋼の機械的性質
- 展伸用マグネシウム合金の材料強度特性
- 金属材料の表面改質による疲労強度の向上
- 超軽量マグネシウム展伸用合金Mg-7Li-0.8Alの機械的性質
- 鍛造焼入れした大型トラック用部品の材料強度特性