Study on the Fatigue Crack Growth Problem under Mode I+II Mixed Mode Condition with Elastic-Plastic Deformation(<Special Issue>Advanced Technology of Experimental Mechanics)
スポンサーリンク
概要
- 論文の詳細を見る
The fatigue crack growth test under mode II dominant condition is conducted. It is found that the crack growth direction can not be predicted by the conventional method. By the fracture surface observation, it is also found that the thickness effect strongly affects this behavior. Three dimensional elastic-plastic FEM analyses are conducted for this problem considering the Bauschinger effect. The change of the crack tip stress field during fatigue crack growth is studied. The criteria to predict the fatigue crack growth direction are studied and new criteria are discussed.
- 一般社団法人日本機械学会の論文
- 2004-07-15
著者
-
Kikuchi Masanori
Mechanical Engineering Department Faculty Of Science And Technology Tokyo University Of Science (rik
-
SATO Toshiaki
Mechanical Engineering Department, Faculty of Science and Technology, Tokyo University of Science (R
-
Sato Toshiaki
Mechanical Engineering Department Faculty Of Science And Technology Tokyo University Of Science (rik
関連論文
- Study on the Fatigue Crack Growth Problem under Mode I+II Mixed Mode Condition with Elastic-Plastic Deformation(Advanced Technology of Experimental Mechanics)
- OS12(4)-14(OS12W0362) Study on the Low Cycle Fatigue Crack Growth Problem under Mode I+II Mixed Mode Condition