Syntheses and thermostabilities of N-substituted maleimide copolymers. IV. terpolymers obtained from N-cyclohexylmaleimide, styrene and acrylonitrile
スポンサーリンク
概要
- 論文の詳細を見る
In order to improve the thermostabilities of copolymers obtained from acrylonitrile (AN) and styrene (ST), so called AS resin, terpolymerization of N-cyclohexylmaleimide (CHMI) was achieved with ST and AN in the presence of radical initiator in benzene at 60℃. The obtained terpolymer had much better thermostabilities than the general AS resin. Weight loss and glass transition temperatures (T_g) of the terpolymers were 10 to 30℃ higher than those of general AS resin. Number-average molecular weights and polydispersity of terpolymers were 1.7×10^5 to 3.4 x 10^5 and 1.7 to 2.3, respectively.
- 山口大学の論文
著者
-
Oishi T
Industrial Chemistry Technical College
-
Fujimoto Minoru
Industrial Chemistry Technical College
-
Oishi Tsutomu
Industrial Chemistry Technical College
-
MOMOI Masaaki
Industrial Chemistry, Technical College
-
HARUTA Yukinori
Nippon Oil & Fats Co., Ltd.
-
Momoi Masaaki
Industrial Chemistry Technical College
-
Haruta Yukinori
Nippon Oil & Fats Co. Ltd.
関連論文
- Syntheses and Thermostabilities of N-Substituted Maleimide Copolymers. III. N-lsopropylmaleimide, N-sec-Butylmaleimide and N-tert-Butylmaleimide
- Syntheses and thermostabilities of N-substituted maleimide copolymers. IV. terpolymers obtained from N-cyclohexylmaleimide, styrene and acrylonitrile
- Reactivities of alkyl N-(4-substituted pheny1) itaconamates in the radical copolymerizations with styrene or methy1 methacrylate