Ti-35Al-15V合金β相の相変態(I) : 電気抵抗測定による相変態過程の追跡
スポンサーリンク
概要
- 論文の詳細を見る
Transformation in quenched ft phase of a Ti-35at%aAl-15at%V alloy has been studied by electrical resistivity measurement. Temperature dependence of the resistivity was examined in temperature range from 50 to 920℃. With a rise in temperature, the resistivity decreased at lower than 300℃, while it increased in the range at 300 to 350℃. Resistivity change of the alloy by isothermal aging was examined at near 300℃. After an incubation period, the resistivity increased with elapsed time and then approached to saturation. These results suggest the metastable ft phase of the alloy happens a phase transformation at near 300℃. In addition, this transformation gives rise to a decrease in hardness of the alloy. This process is sensitive to a temperature change. The activation energy for this process is estimated based in its temperature dependence.
- 函館工業高等専門学校の論文
著者
-
田淵 正幸
函館工業高等専門学校一般科目理数系
-
外崎 修司
函館工業高等専門学校機械工学科
-
桶谷 健太
函館工業高等専門学校機械工学科
-
桶谷 健太
函館工業高等専門学校機械工学科: (現)室蘭工業大学
-
外崎 修司
函館工業高等専門学校機械工学科: (現)旭テック株式会社
関連論文
- 電子顕微鏡像の干渉縞を利用したCu-Zn-Al合金ベイナイトの変態歪の解析
- Cu-Zn-Al合金β_1相におけるベイナイト変態と平衡α相への相変態の温度依存性
- Ti-Al-V合金の電気抵抗率の温度依存性
- Ti-35Al-15V合金β相の相変態(I) : 電気抵抗測定による相変態過程の追跡
- Ti-40Al-10V合金の引張特性
- Ti-Al-V合金の電気抵抗特性
- LabVIEWによる電気抵抗測定システムの作製