マッシブなコンクリートの強度発現傾向 : セメントの水和熱の蓄積による高温履歴の影響
スポンサーリンク
概要
- 論文の詳細を見る
Recent developments of concreting in Japan yielded many considerations. One of them is the trend in constructing building in large dimensions ; for example, the construction of power plants, particularly nuclear power plants requise huge shiedings, i. e. , very large-dimension mass concrete. The process of concreting is based on temperature, i. e. , the heat of hydration and consequently the emerged compressive strength. This papar provides analysis of the results of about 70 expenmental works conducted and published in Japanese over the past 10 years on concreting processes and the conclusions could be summerized as follows ; The strength of core-test specimen provides that strength achieved, with high concreting temperature remains constant or rather with slight increase after initial rise at the first phase, while strength at low-concreting temperature increases in respect of time, i. e. , age measured in terms of months.
- 社団法人日本建築学会の論文
- 1992-06-30
著者
関連論文
- 日本各地の温湿度変化に影響を及ぼす都市化環境要因 : 都市気候を考慮した市街地の緑地整備量に関する基礎的研究 その2
- プレキャスト複合コンクリート工事の合理化と問題点(材料施工部門 パネルディスカッション)(1999年度日本建築学会大会(中国))
- 1304 シリカフォームを用いた超高強度コンクリートの応力・ひずみ曲線に関する実験 : その2. 応力・ひずみ曲線について
- 1303 シリカフォームを用いた超高強度コンクリートの応力・ひずみ曲線に関する実験 : その1. 圧縮強度、弾性係数及びポアソン比について
- 1380 高強度プレキャストコンクリート製造時の温度履歴と強度発現性状の関係 : その5.早強ならびに低発熱型セメントを用いた模擬部材の強度性状
- 1379 高強度プレキャストコンクリート製造時の温度履歴と強度発現性状の関係 : その4.早強ならびに低発熱型セメントを用いた模擬部材の温度履歴
- 1368 低発熱型セメントを用いたコンクリートの中性化に関する研究 : その2. 中性化速度係数およびフライアッシュ特性
- 1367 低発熱型セメントを用いたコンクリートの中性化に関する研究 : その1. 圧縮強度および中性化深さ
- 産業廃棄物を封入するための超高性能マイクロコンクリート (材料・施工)(文献抄録)
- セメントペーストと骨材の接触領域に及ぼす無機混和材の影響に関するシミュレーション, Dale P.Bentz and Edward J.Garboczi : Simulation Studies of the Effects of Mineral Admixtures on the Cement Paste-Aggregate Interfacial Zone [ACI, Materials Journal, Vol.88, No.5, "9109-9110", pp.518-528, 図10,表3](材