Ti-6Al-4Vの疲労き裂伝播限界に及ぼす高真空環境の影響(J10-1 チタン系材料の力学・強度特性,J10 チタン系材料の力学・強度特性と応用技術)

概要

論文の詳細を見る
Uniaxial tension fatigue tests were carried out in air and in high vacuum environments using test pieces made of Ti-6Al-4V with small artificial defects. We examined environmental effects of high vacuum on S-N properties and fatigue crack growth limit. As a result, the following were obtained, (i) Regardless of defect sizes, fatigue lives in high vacuum were much longer than those in air. The slope of S-N curve showed different tendencies between in air and in high vacuum corresponding to defect sizes, (ii) The downward trend of ΔK_<th> with decreasing crack size existed not only in air but also in high vacuum, and the tendency was stronger in high vacuum than in air.
社団法人日本機械学会の論文
2004-09-04