Microstructural Analysis of Interface Between YBa_2Cu_3O_<7-X> and Ag/Pd Alloys

スポンサーリンク

概要

• 論文の詳細を見る

• Pure silver and palladium/silver alloy in a 10/90 weight ratio were either sandwich-coupled or powder-mixed with YBa_2Cu_3O_<7-X> (Y123) to prepare Ag-Y123 and (Pd/Ag)-Y123 composites. The reaction and diffusion of elements near the interface of Ag-Y123 or (Pd/Ag)-Y123 were determined by means of differential thermogravimetry (DTA), optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS), and precision X-ray diffraction (XRD) analyses. The results reveal that the Pd, Ag, and Cu react to some extent: Cu will diffuse into pure Ag or Pd/Ag alloy. Conversely, Pd and Ag in pure Ag or Pd/Ag will diffuse toward Y123 at temperatures greater than 945℃. Diffusion of Cu into pure Ag or Pd/Ag alloy will decrease the melting point of the Ag or Pd/Ag alloy due to formation of a solid solution and/or an eutectic constitution. Since molten Cu/Ag or Cu/Pd/Ag alloys can flow across the interface by means of capillary force between Y123 grains, they fill up the voids (or capillaries) between Y123 grains and Ag or Pd diffuse into Y123 grains, occupying Cu sites in Y123. This is consistent with the results of precision XRD, which show the expansion of the Y123 lattice caused by the occupation.

• 社団法人応用物理学会の論文
• 1993-10-15

著者

• Wei Wen-cheng

  Institute Of Materials Science And Engineering

• Wei Wen-cheng

  Institute Of Materials Science And Engineering National Taiwan University

• LO Ming-Hung

  Institute of Materials Science and Engineering, National Taiwan University

• Lo Ming-hung

  Institute Of Materials Science And Engineering National Taiwan University

関連論文

• SiCのコロイドプロセッシングと液相焼結
• 乾燥調節剤を用いた超微粒子アルミナケーキの乾燥の動力学
• Microstructural Analysis of Interface Between YBa_2Cu_3O_ and Ag/Pd Alloys
• Grain Delamination of Ag-Doped YBa_2Cu_3O_ Superconductor

スポンサーリンク