直流通電によるコンクリートの脱水効果 (その 2)
スポンサーリンク
概要
- 論文の詳細を見る
In the present paper experimental studes on driect electric curing is reported continuously in part I of this paper. Experimental studies was carried out with experimentatic programing L_18 (2^1+3^7) type on the subject of the reasonable specification about extractation of water and its the necessary time from concrete, temperature of concrete, and economy on a cut of electric power consumption. Reasonable specification on electric curing of concrete was decided by result of each work. Experimental primary factor are kind of aggregates (natural aggregate, natural light weight aggregate artificial light weight aggregate), kind of cements (portland cement, silica cement, portland blast furnace cement), activity agent (vinsol, pozzolis), sand aggregate ratio (35, 40, 45), volume of cement (230, 250, 270kg/m^3), volume of water (150, 170, 190l/m^3), and electric current (1A, 2A, 3A). Result of work, effect of current have the most favorable influence on it. Resonable specification on electric curing of concrete is such that; concrete is produced by portland blast furnace cement and its proportion is 210〜230kg/m^3. Proportion of water is 190l/m^3 and of sand aggregate ratio is 35〜45 percentage. Electric current is 1A (0.1 A/cm, 0.025 A/cm^2). Ion is educed from cathode plate by direct electric current. Volume of educe is calibrated by Faradey's Law. 6g of lead per 1g equivalence is educe. Chemical constituent of cohesion is shown table 4.
- 一般社団法人日本建築学会の論文
- 1969-10-30
著者
関連論文
- 骨材の電気化学的性質 : 膜電位
- 直流通電によるコンクリートの電気分解と電気重合
- 直流通電によるコンクリートの脱水度に関する理論解析
- 直流通電によるコンクリートの脱水効果 (その 3)
- 直流通電によるコンクリートの脱水効果 (その 1)
- 塗り床用エポキシ樹脂の施工の仕様とその確認の方法に関する実験
- コンクリート製造における減圧加水効果に関する実験的研究
- 骨材の電気化学的性質 : 流動電位
- 骨材の電気化学的性質 : 膜電位
- コンクリート用骨材とセメントペーストとの付着に関する実験的研究
- 1012 骨材の流動電位(材料・施工)
- 直流通電によるコンクリートの脱水効果 (その 2)