2号塗膜中に含まれる防汚剤の溶出挙動について (第3報)
スポンサーリンク
概要
- 論文の詳細を見る
Antifouling paint on the shell bottom performs functions of making the surface of the shell bottom smooth and preventing an increase in frictional resistance by preventing the attachment of marine growth thereto. For three kinds of antifouling paints different in antifouling system, we have carried out a rotor test in sea water, and measured the surface roughness by using a surface roughness gauge and observed the paint film cross section by an electron scanning microscope. In regard to the leaching behaviour of antifouling agent and the change of paint film surface condition, the following results have been found : 1) The leaching rate of antifouling agent obtained in the rotor test in sea water is 70-150 times that in immersion test in still sea water. 2) To prolong the life of antifouling paint, it is effective to control the diffusion of antifouling agent in paint film. 3) In such conditions as in the rotor test in sea water, the surface roughness hardly changes. Thus, we have confirmed that this investigation is useful to clear the relation between the leaching behaviour of antifouling agent and the antifouling performance.
- 社団法人日本船舶海洋工学会の論文
- 1979-09-30
著者
関連論文
- 2号塗膜中に含まれる防汚剤の溶出挙動について
- 鉄筋コンクリート中の鉄筋の腐食に関する試験法 (腐食防食小特集)
- 477 耐候性鋼を使用した大型海上橋の腐食量について(海洋構造物の腐食と防食・破壊と疲労, 加工・システム・利用技術, 日本鉄鋼協会第 112 回(秋季)講演大会)
- 340 レーザービームを利用したNi基自溶性合金被覆の性能
- 2号塗膜中に含まれる防汚剤の溶出挙動について (第3報)
- 2号塗膜中に含まれる銅の溶出挙動について
- 造船塗装工程の短縮に関する一実験
- 船舶用タールエポキシ樹脂塗料の層間付着性について
- 12 腐食事故の調査
- 船舶および海洋構造物の防食
- 素地調整条件と塗膜性能に関する一考察
- 塗装によるカーゴオイルタンクの防蝕について