歯科用Ni-Cr合金のレーザ溶接部の割れ : 合金組成の影響

概要

論文の詳細を見る
For the purpose of clarifying the effect of alloy compositions on cracking in laser welds of dental Ni-Cr alloys, 12 commercial and 11 experimental Ni-Cr alloys for crown and bridges were subjected to pulsed YAG laser spot welding, and their welds were investigated by optical and scanning electron microscopy, and EDX and thermal analysis methods. Main conclusions are as follows. 1. Cracks in laser welds were solidification cracks at grain boundaries in weld fusion zones. 2. In the case of commercial dental Ni-Cr alloys, a considerable number of eutectics enrichedin Si, Al and/or S were formed. Greater cracking susceptibility was interpreted by considering that these eutectics solidified at solidification temperatures far lower than the nominal solidus. 3. In the case of experimental Ni-Cr allows with a small amount of eutectics, S and Si enhanced cracking sensitivity, but Mn reduced cracking. 4. The above results suggest that it is beneficial to the prevention or reduction of cracking to decrease harmful elements such as Si and S forming low solidification temperature eutectics or to add some elements such as Mn forming higher solidification temperature eutectics instead of lower ones.
社団法人日本補綴歯科学会の論文
1990-06-01