ワックス・クラウン作製操作時の外力にともなう寸法変化についての実験的研究
スポンサーリンク
概要
- 論文の詳細を見る
This experimental study has been performed to investigate the distortion of wax patterns caused by the loading force, and to examine the influence of the angle of the axial wall of the crown, the kind of inlay wax, and the manipulation for waxes on the distortion. a) Wax patterns for crowns were made on the plaster dies, employing metal original dies. The axial dimensional change caused by the loading force on the occlusal surface and the axial wall of the wax patterns was measured by use of the optical fiber transducer for detection. b) The metal sprue pin 2mm in diameter was inserted in the centter of the occlusal surface, and the tension produced when the sprue pin was pulled out was measured. The results obtained were as follows : (1) A large amount of distortion on the axial surface of the wax pattern caused by the vertical load at the central region was observed at the occlusal, central, or marginal region. Furthermore, the distortion of both the occlusal and marginal regions was conspicuous in comparison with that in the central region, and a concave-shaped distortion wasfound on the axial surface. (2) Concerning the relationship between the distortion, which was brought about when the wax pattern was pressed between the thumb and index finger, and the duration which was left after the preparation of the wax pattern, the distortion observed when the wax pattern was left at 1 hour or 24 hours after taking off was smaller in amount than that observed immediately there after. (3) The tension loaded for pulling out the wax patterm from the plaster die was approximately 3 kg,and the axial surface of the wax pattern was noticed to shrink.
- 社団法人日本補綴歯科学会の論文
- 1982-12-01