相変態が応力集中部の応力緩和特性におよぼす影響 : 変態超塑性による応力緩和(第6報)

概要

論文の詳細を見る
Residual stresses and angular distorsions are very important probrems in welding design and fabrication. In the previous reports_<2,3)> it was shown that the materials with a martensitic transformation at low temperature were effective to the reduce residual stress and anguler distorsion in welding. In this report the effects of transformation on prevention against crack in welding were examined by use of restraint thermal cycle test and constraint crack test. The results are shown as follows ;(1) The materials with transformation at low temperature were effective to reduce residual stresses in stress concetration area and to prevent cracks in welding.(2) As the result of the stress consentration test (mild steel was broken in the midst of cooling by this test method), it was possible to prevent a crack or a failure at the stress concentration area by use of the materials with the transformation at low temperature. In this case, the transformation superplasticity was more effective than transformation expansion to release the stress concentration.(3) The M_s temperature of the materials with the transformation at low temperature (there was no crack by use of these materials in this test) was less than 200℃. But a dilution from a base metal raised the transformation temperature and the free thermal contraction curve changed. Therefore in welding practices, the change of transformation temperature by the dilution from base metal is also important.
社団法人溶接学会の論文
1993-11-05

相変態が応力集中部の応力緩和特性におよぼす影響 : 変態超塑性による応力緩和(第6報)

スポンサーリンク

概要

著者

関連論文

スポンサーリンク