溶融亜鉛めっき鋼板の点溶接
スポンサーリンク
概要
- 論文の詳細を見る
The use of zinc-coated steel sheets in industries has increased rapidly. Spot welding of galvanized steel sheets, however, has been a problem from the beginning. That is poor electrode life due to high welding current. An attempt has been made in this program to improve weld quality deterioration in the spot welding of galvanized steel sheets. Aluminum oxide powder is interposed at the interface between two galvanized steel sheets to be welded, having an aim to increase contact resistance at faying surface. Tests have indicated that the powder addition is much effective to reduce weld time requirements and consequently, for improving tip life and welding performance.
- 1988-11-05
著者
関連論文
- オーステナイト系ステンレス鋼溶接金属の不均一変形挙動
- 溶接部ならびに鋳物の透過 X 線写真にあらわれる影(第 6 報) : 影と高温延性(溶接部のミクロ・フラクトグラフィ)
- 溶接部ならびに鋳物の透過 X 線写真にあらわれる影(第 2 報) : 溶接条件と影
- 449 ステンレス溶接金属の透過X線写真にあらわれる影 : 溶接条件と影
- 316 ステンレス溶接金属の透過X線写真にあらわれる影 : 影と高温延性について
- 溶融亜鉛めっき鋼板の点溶接
- 溶接部ならびに鋳物の透過 X 線写真にあらわれる影(第 5 報) : 影と延性
- 357 溶接金属および鋳物の透過X線写真にあらわれる影 : 影と引張強さ
- 431 ステンレス溶接金属の透過X線写真にあらわれる影 : 影と曲げ延性
- 202 ステンレス溶接金属の透過X線写真にあらわれる影 : 影におよぼす長時間溶体化処理の影響
- 235 溶接部の透過X線写真にあらわれる影 : 軟鋼溶接部の場合
- ステンレス鋼溶接部の成分偏析と透過X線写真にあらわれる影(昭和62年度春季全国大会論文発表講演討論記録)
- ステンレス鋼溶接部の成分偏析と透過X線写真にあらわれる影(平成62年度春季全国大会論文発表講演論文)
- 低炭素鋼溶接部の透過X線写真にあらわれる影と溶接部の機械的性質
- 低炭素鋼溶接部の透過X線写真にあらわれる影と延性
- オ-ステナイト系ステンレス鋼溶接部の透過X線写真にあらわれる影--溶接部の内部ひずみ量とδフェライト
- 234 溶接部ならびに鋳物の透過X線写真にあらわれる影 : 影とラウエはん点
- オ-ステナイト系ステンレス鋼溶接部の透過X線写真にあらわれる影--影のコントラストにおよぼす結晶粒度の影響
- 315 ステンレス溶接金属の透過X線写真にあらわれる影 : 影と疲労強度について
- 溶接部ならびに鋳物の透過 X 線写真にあらわれる影(第 4 報) : 溶接割れと影
- 溶接部ならびに鋳物の透過 X 線写真にあらわれる影(第 3 報) : 結晶粒界と影
- 225 ステンレス溶接部の透過X線写真におらわれる影 : 硫黄添加の影響について
- オーステナイト系ステンレス鋼鋳物ならびに溶接金属の密度
- 溶接部ならびに鋳物の透過 X 線写真にあらわれる影(第 1 報) : 影の形態とその特長
- 344 ステンレス溶接金属ならびに鋳物の密度
- 441 溶接割れならびにスリットによる影 : 溶接部の透過X線写真にあらわれる影.第3報
- 440 影の微細構造 : 溶接部の透過X線写真にあらわれる影.第2報
- 439 影の形態とその特長 : 溶接部の透過X線寫真にあらわれる影.第1報