スポット溶接継手の疲れ強さ : 疲れ強さにおけるピッチの影響
スポンサーリンク
概要
- 論文の詳細を見る
To ascertain the effects of the pitch of spots on the fatigue strength, two kinds of spot welded joints with pitches of 10-60mm were tested under pulsating tensile loads (stress ratio 0). The first was made by lapping and joining two stainless steel plates and was named SUS+SUS. The second was made of a stainless steel plate and a carbon steel plate lapped and joined together, SUS+SPC. In order to explain the relation between the pitch and the fatigue strength of joints, also studied were the effect of the pitch on the welding consequences (nugget size, structure of heat affected zone and welding residual stress) and the relation between the pitch and stress concentration at the nugget edge where the joints failed due to fatigue. In the results of fatigue test, the fatigue strength expressed by the load per one spot, at any life, was not necessarily constant but had a tendency to lower as the pitch became smaller. In SUS+SPC joints, fatigue ratio (fatigue strength/tensile strength) was approximately constant regardless of the pitch. In SUS+SUS joints the ratios for lives up to (10)^6 cycles were also constant, for longer lives over (10)^6 cycles, however, the ratios decreased with an increase of the pitch. Effects of the pitch on the consequences of welding were obtained as follows. Concerning the size of nugget and the microstructure of heat affected zone around the nugget, no considerable differences by the pitch were observed. However, concerning residual stress caused by welding which was measured by X-ray diffraction ((sin)^2 ψ method), the differences due to the pitch were great. For instance, the residual stress at the nugget edge was estimated about 39kg/(mm)^2 with a pitch of 60mm, while it was about 24kg/(mm)^2 with one of 20mm (for SUS+SUS joints). By stress measurement with electric wire strain gauges and stress analysis, relations between the stress concentration at nugget edge and the pitch were obtained. In this result for SUS+SUS joints, the stress concentration with a pitch of 60mm was about 2.4 times as that for 20mm pitch. Taking the residual stress and the stress concentration at nugget edge into consideration on the fatigue strength at (10)^7 cycles for SUS+SUS joints, for any pitches, the maximum stress of stress cycle at nugget edge was approximately identical to the proof stress of the base material, and so it was pointed out that the effect of the residual stress on fatigue strength was very important.
- 社団法人溶接学会の論文
- 1967-07-25
著者
関連論文
- 高温塑性疲れに関する一実験 : その4,き裂に着目した疲れ過程を進ませる因子とき裂の性質について
- 高温塑性疲れに関する一実験(その4、き裂に着目した疲れ過程を進ませる因子とき裂の性質について)
- 高温塑性疲れに関する一実験 : その3,き裂に着目した疲れ過程における温度,塑性ひずみ幅の影響について
- 高温塑性疲れに関する一実験 : その2,破断時のき裂の状態に着目しての温度, 繰返し速度の影響
- 高温塑性疲れに関する一実験 : その1,破断繰返し数を支配する因子について
- 高温塑性疲れに関する一実験 : その2, 破断時のき裂の状態に着目しての温度, 繰返し速度の影響
- 高温塑性疲れに関する一実験 : その1, 破断繰返し数を支配する因子について
- 熱疲れに関する一実験 : き裂に着目した熱疲れ過程に関する一考察
- 熱疲れに関する一実験 : 温度および拘束熱ひずみの影響
- 熱疲れに関する一実験 : き裂に着目した熱疲れ過程に関する一考察
- 熱疲れに関する一実験 : 温度および拘束熱ひずみの影響
- 78 高張力鋼の溶接継手の疲労強度算定法
- スポット溶接継手の疲れ強さ : 疲れ強さにおけるピッチの影響
- (21) 薄鋼板のスポット溶接継手の疲れ強さ(第 2 報)
- (24) 薄鋼板のスポット溶接継手の疲れ強さ(第 1 報) : 1 点継手と横 1 列 4 点継手の疲れ強さについて(昭和40年春季全国大会講演概要)