硬ロウおよびロウ付接合部の衝撃強さ
スポンサーリンク
概要
- 論文の詳細を見る
As to impact-strength of brazed joints, there have been a few reports. They have not explained the relation between the impact strength of filler metals and that of the joints brazed with them, and also have not proved the state of fracture in brazed joint whose base metals as copper and copper alloys were weaker than filler metals. Authors investigated the relation between charpy impact-strength of filler metals and brazed joints using eight kinds of filler metals in Ag-P-Cu and Ag-Cu-Zn-Cd types and copper base metal. And we studied the fracture mechanism for various brazed joints, the effects of annealing for various filler metals and brazed joints and the influences of joint thickness in brazed joints for the impact strength. The test results summarized as follows : 1) The impact-strength of filler metals in Ag-Cu-Zn-Cd type were stronger than that in Ag-P-Cu type and the impact-strength of both filler metals was improved by increase of silver contents in filler metals. 2) The impact-strength of brazed copper joints was generally less than those of filler metals and it was determined by the impact-strength of filler metals. 3) The fracture crack in impact specimens of brazed copper joints whose filler metals had higher impact-strength than base metal began from the boundary layer between filler metal and base metal. But, the fracture crack of brazed joints whose filler metals had less impact-strength than base metals began from filler metals. As a result, the absorbed energies in brazed joints had a large difference with both brazed joints. 4) After diffusion annealing, impact-strength of brazing filler metals and brazed joints became weak in Ag-P-Cu type and strong in Ag-Cu-Zn-Cd type. 5) When impact-strength of filler metals was higher than that of base metals, the thickness in brazed joints had no effect on impact-strength of filler metals was weaker than that of base metals, the joint thickness gave some influences to impact-strength.
- 社団法人溶接学会の論文
- 1964-08-25
著者
関連論文
- 銅および銅合金に対する硬ロウのぬれ性
- 銅の硬ロウ付接合部の引張強さ
- 硬ロウ材の高温機械的性質について
- (108) 硬ロウ付に関する研究(第 3 報) : ロウ付接合部の引張強さ(昭和 38 年度秋季全国大会講演概要)
- (85) 硬ロウ付に関する研究第 2 報 : 硬ロウの流動性(昭和 37 年度秋季全国大会講演概要)
- (84) 硬ロウ付に関する研究(第 1 報) : 硬ロウ材の高温機械的性質(昭和 37 年度秋季全国大会講演概要)
- 硬ロウおよび銅のロウ付接合部の耐蝕性
- ロウ付接合部の常温および高温疲労強さ
- (67) 硬ロウ付に関する研究(第 7 報) : ロウ接合部の常温および高温疲れ強さ
- 硬ロウおよびロウ付接合部の衝撃強さ
- 硬ロウ付部の剪断強さ
- (111) 硬ロウ付に関する研究(第 6 報) : ロウおよび接合部の耐蝕性(昭和 38 年度秋季全国大会講演概要)
- (110) 硬ロウ付に関する研究(第 5 報) : ロウ付接合部の剪断強さ(昭和 38 年度秋季全国大会講演概要)
- (109) 硬ロウ付に関する研究(第 4 報) : ロウおよび接合部の衝撃強さ(昭和 38 年度秋季全国大会講演概要)